Failure analysis of the brass tubes in a lubricating oil cooler

被引：14

作者：

Qu, S. ^{[1
]}

Yao, G. ^{[1
]}

Tian, J. F. ^{[1
]}

Zhang, Z. F. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Met Res, Shenyang Natl Lab Mat Sci, Shenyang 110016, Peoples R China

来源：

ENGINEERING FAILURE ANALYSIS | 2011年 / 18卷 / 08期

关键词：

Lubricating oil cooler; Brass tubes; Pit; Dezincification; Stress corrosion cracking (SCC);

D O I：

10.1016/j.engfailanal.2011.07.018

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

Failure analysis was carried out on leaked brass tubes of a lubricating oil cooler. Direct evidences of dezincification and stress corrosion cracking (SCC) were observed by scanning electron microscope (SEM) and energy dispersive spectroscopic (EDS) analysis. It is found that there are many small pits distributed on the fracture surface and EDS analysis revealed the occurrence of dezincification in the small pits. SCC was observed on the cross-sectional plane of the fracture by SEM. Ammonia test has proved the existence of residual stress in the as-received tubes. It is determined that the brass tubes have been suffered from the coaction between dezincification and SCC. (C) 2011 Elsevier Ltd. All rights reserved.

引用

页码：2232 / 2239

页数：8

共 50 条

[21] Failure analysis of oil tubes attached to ethylene compressor
Wang, Qiongqi
Xuan, Fu-Zhen
Wang, Zhengdong
TRANSFERABILITY AND APPLICABILITY OF CURRENT MECHANICS APPROACHES, 2009, : 473 - 477
[22] Failure analysis of admiralty brass tubes in a surface condenser: a case study at the petrochemical industry
Ardy, Husaini
Nurimam, Asep
Hamdani, Mohammad
Abednego, Try Hutomo
Helmy, Rizky Kurnia
Bangun, Deri Andika
Setiawan, Asep Ridwan
Wibowo, Arie
Sumboja, Afriyanti
MATERIALS AT HIGH TEMPERATURES, 2021, 38 (03) : 177 - 185
[23] Fault Tree Analysis of Vehicle Engine Lubricating Oil's Failure
Han Qilong
Gao Xin
MECHATRONICS AND APPLIED MECHANICS II, PTS 1 AND 2, 2013, 300-301 : 172 - 175
[24] Failure assessment of composite cooler tubes in a gas boosting station
Ranjbar, Khalil
ENGINEERING FAILURE ANALYSIS, 2011, 18 (01) : 192 - 201
[25] Failure analysis of X-Msn oil cooler fan blade on helicopter
Hwang, Young-Ha
Kim, Tae-Gu
ENGINEERING FAILURE ANALYSIS, 2009, 16 (06) : 1991 - 1995
[26] Application of grey relational analysis for corrosion failure of oil tubes
Fu, CY
Zheng, JS
Zhao, JM
Xu, WD
CORROSION SCIENCE, 2001, 43 (05) : 881 - 889
[27] Effect of lubricating oil on prevention of rippling failure
Nohara, Minoru
Nagamura, Kazuteru
Ikejo, Kiyotaka
Matsuo, Kouhei
Nippon Kikai Gakkai Ronbunshu, C Hen/Transactions of the Japan Society of Mechanical Engineers, Part C, 2002, 68 (08): : 2444 - 2450
[28] FAILURE ANALYSIS OF A TRANSFORMER OIL COOLING TUBE MADE OF ALPHA-BRASS
KUMAR, S
SAH, DN
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 1992, 45 (05): : 343 - 345
[29] Wear failure analysis of ball bearings based on lubricating oil for gas turbine
Sun, Jiasi
Bu, Jiali
Yang, Jinglai
Hao, Yanlong
Lang, Hong
INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2023, 75 (01) : 36 - 41
[30] Cause Analysis of Plate Pitting Corrosion in Lubricating Oil Cooler of Main Equipment in Datang Weihe Thermal Power Plant
Li, Zhouping
Hu, Xiaojian
Ma, Haiyan
Yan, Siwei
Yan, Aijun
Feng, Lajun
ADVANCES IN CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING, PTS 1-5, 2013, 634-638 : 1677 - 1681

← 1 2 3 4 5 →