Critical current density and irreversibility line in melt-textured YBCO with CeO2 addition

被引：0

作者：

Lee, KW ^{[1
]}

Kim, CJ ^{[1
]}

Park, YK ^{[1
]}

Park, JC ^{[1
]}

机构：

[1] KOREA ATOM ENERGY RES INST,TAEJON 305600,SOUTH KOREA

来源：

CHINESE JOURNAL OF PHYSICS | 1996年 / 34卷 / 02期

关键词：

D O I：

暂无

中图分类号：

O4 [物理学];

学科分类号：

0702 ;

摘要：

We prepared melt-textured YBCO with CeO2 addition in order to enhance flux pinning. SEM photographs showed that Y2BaCuO5 precipitates of about 1 mu m size were uniformly distributed in YBCO grains. Magnetization hysteresis at various temperatures was measured to investigate critical current density using a SQUID magnetometer. Critical current density at 77 K in a field of 1 T was about 2 x 10(4) A/cm(2) and increased by lowering temperature. The irreversibility line determined from the closing points of the magnetization hysteresis was shifted to high fields. The temperature dependence of the irreversibility field followed a power law, H-irr proportional to (1-T/T-c)(n) with n approximate to 1.4.

引用

页码：702 / 705

页数：4

共 50 条

[31] Dependence of critical current density on the oxygen content for Y-123 single domain melt-textured samples
Murashov, VA
Horvat, J
Ionescu, M
Liu, HK
Dou, SX
APPLIED SUPERCONDUCTIVITY 1997, VOLS 1 AND 2: VOL 1: SMALL SCALE AND ELECTRONIC APPLICATIONS; VOL 2: LARGE SCALE AND POWER APPLICATIONS, 1997, (158): : 869 - 872
[32] Preparation of melt-textured YBa2Cu3O7-δ bulk with CeO2 additions and their superconducting properties
Takagi, A
Miyamoto, T
Ikuta, H
Mizutani, U
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 412 : 586 - 591
[33] EBSD characterisation of Y2Ba4CuUOx phase in melt-textured YBCO with addition of depleted uranium oxide
Koblischka-Veneva, A.
Muecklich, F.
Koblischka, M. R.
Babu, N. Hari
Cardwell, D. A.
7TH EUROPEAN CONFERENCE ON APPLIED SUPERCONDUCTIVITY (EUCAS'05), 2006, 43 : 438 - 441
[34] Microstructure of melt-textured Y-Ba-Cu-O oxides with CeO2 addition and the formation mechanism of the Ba-Cu-O platelet structure
Kim, CJ
Kim, KB
Park, HW
Sung, TH
Kuk, IH
Hong, GW
SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1996, 9 (02): : 76 - 87
[35] Microstructure of melt-textured Y-Ba-Cu-O oxides with CeO2 addition and the formation mechanism of the Ba-Cu-O platelet structure
Korea Atomic Energy Research Inst, Taejon, Korea, Republic of
Supercond Sci Technol, 2 (76-87):
[36] CRITICAL CURRENT DENSITIES OF MELT-TEXTURED YBA2CU3O7-Y
FAN, HC
ZHANG, YT
JIN, X
LU, M
JI, HL
XU, XN
YAO, XX
REN, HT
XIAO, L
HE, Q
PHYSICA C, 1991, 185 : 2331 - 2332
[37] ENHANCED CRITICAL-CURRENT DENSITY IN MELT-TEXTURED (Y1-XPRX)BA2CU3OY
REN, HT
TAYLOR, KNR
CHEN, YJ
XIA, JA
QING, H
PHYSICA C, 1993, 216 (3-4): : 447 - 452
[38] CRITICAL-CURRENT DENSITY OF A SAMPLE OF MELT GROWN YBCO
GANESAN, V
SRINIVASAN, R
GOPALAN, R
RAJASEKARAN, T
SOLID STATE COMMUNICATIONS, 1993, 87 (11) : 1077 - 1080
[39] Deposition and characterization of YBCO/CeO2/YSZ/CeO 2 multilayers on biaxially textured Ni substrates
Physics and Technology College, Hebei University, Baoding 071002, China
不详
Chin. Phys., 2006, 2 (444-448):
[40] COMPARISON BETWEEN THE MAGNETIC AND TRANSPORT CRITICAL CURRENT DENSITIES IN HIGH CRITICAL CURRENT-DENSITY MELT-TEXTURED YTTRIUM BARIUM COPPER-OXIDE
GAO, L
MENG, RL
XUE, YY
HOR, PH
CHU, CW
APPLIED PHYSICS LETTERS, 1991, 58 (01) : 92 - 94

← 1 2 3 4 5 →