Efficient PVD-coatings for roller bearings

On the basis of cylindrical roller thrust bearings it was systematically examined to what extent PVD-coatings are able to take over the function of EP/AW-additives. The bearings were tested under heavy-duty conditions in order to distinguish very fast the efficiency of different coating-substrate-systems. Several coatings were tested for their ability to protect an un-coated counterpart. So just the washers of the roller bearings were coated, the rollers stayed un-coated. Four Me-C:H-coatings showed the best performance and fulfilled the required criterion for roller bearings in the boundary friction: low loss of mass and hardly surface deviation. Material carryover from the carbonaceous coating to the 100Cr6 steel surface was developed by the Me-C:H-coatings during the tests. This mechanism was able to protect the un-coated rollers. Closer investigations were done with an ESMA analysis (electron beam micro range analysis) on ZrCg-coatings. It could be seen, that a reaction layer was formed on the rollers. This layer contained remarkable masses of zirconium and oxygen.