Evaluation of precursors for DLI MOCVD of ferroelectric BLT

被引:18
|
作者
Kang, SW [1 ]
Rhee, SW [1 ]
机构
[1] Pohang Univ Sci & Technol, Dept Chem Engn, Lab Adv Mol Proc, Pohang, South Korea
关键词
D O I
10.1149/1.1595661
中图分类号
O646 [电化学、电解、磁化学];
学科分类号
081704 ;
摘要
Precursors for the direct liquid injection (DLI) metallorganic chemical vapor deposition (MOCVD) of Bi4-xLaxTi3O12 (BLT) thin films, Bi(phenyl)(3) [Bi(Ph)(3)], Bi(2,2,6,6-tetramethylheptanedionate)(3)[Bi(tmhd)(3)], La(tmhd)(2)-pentamethyldiethylenetriamine) [La(tmhd)(2)-PMDT], and Ti(dimethylaminoethoxide)(4) [Ti(dmae)(4)] were characterized by Fourier transform infrared spectroscopy (FTIR), differential scanning calorimetry, and thermogravimetric analysis. The reactions among Bi, La, and Ti precursors in a single-mixture solution was identified using a H-1-nuclear magnetic resonance spectrometer and it was shown that Bi( Ph) 3 was better than Bi(tmhd)3 as a Bi precursor because Bi(tmhd)(3) reacted with Ti(dmae)(4) in the solvent. The gas phase decomposition temperatures of three precursors, Bi(Ph)(3), La(tmhd)(3)-PMDT, and Ti(dmae)(4) were found with FTIR to be 400, 375, and 325degreesC, respectively. Evaporator temperature was optimized from the deposition rate of the single oxide from each precursor. The deposition behavior could be explained in terms of the precursor characteristics. Fatigue-free and highly c axis oriented BLT thin films were grown on Pt/TiO2/SiO2/Si at the deposition temperature of 400degreesC. For the BLT film annealed at 650degreesC, the remanent polarization (2P(r)) and coercive field (E-c) were 12 muC/cm(2) and 56 kV/cm, respectively. The BLT capacitors did not show any significant fatigue up to 4 x 10(10) cycles at a frequency of 1 MHz. (C) 2003 The Electrochemical Society.
引用
收藏
页码:C573 / C576
页数:4
相关论文
共 50 条
  • [41] Novel precursors for ferroelectric materials
    Boyle, TJ
    Pedrotty, DM
    Tafoya, CJ
    Scott, B
    Ziller, JW
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 1998, 215 : U850 - U850
  • [42] Evaluation of metalorganic precursors for fabrication of lead-based ferroelectric thin films
    Tokita, K
    Okada, F
    FERROELECTRICS, 1998, 211 (1-4) : 127 - 140
  • [43] Syntheses of novel mixed metal alkoxide MOCVD precursors
    Andrews, NL
    Boyle, TJ
    Rodriguez, MA
    Gallegos, JJ
    ABSTRACTS OF PAPERS OF THE AMERICAN CHEMICAL SOCIETY, 2003, 225 : U14 - U15
  • [44] New heteroleptic copper(II) complexes as MOCVD precursors
    Krisyuk, V. V.
    Sysoev, S. V.
    Rumyantsev, Y. M.
    Prokhorova, S. A.
    Maximovskiy, E. V.
    Kosinova, M. L.
    Igumenov, I. K.
    NINETEENTH EUROPEAN CONFERENCE ON CHEMICAL VAPOR DEPOSITION (EUROCVD 19), 2013, 46 : 174 - 182
  • [45] Trimethylphosphite stabilized disilver(I) methanedisulfonates as MOCVD precursors
    Tao, Xian
    Shen, Ke-Cheng
    Feng, Meng
    Tang, Qing-Yun
    Fang, Jiang-Tao
    Wang, Yu-Long
    Shen, Ying-Zhong
    POLYHEDRON, 2011, 30 (16) : 2661 - 2666
  • [46] MOCVD GROWTH OF YBCO USING FLUORIDE BASED PRECURSORS
    BETSCH, RJ
    PANSON, AJ
    CHARLES, RG
    CIFONE, W
    JOURNAL OF ELECTRONIC MATERIALS, 1990, 19 (07) : 51 - 51
  • [47] Vapor pressures of the copper and yttrium β-diketonate MOCVD precursors
    Colominas, C
    Lau, KH
    Hildenbrand, DL
    Crouch-Baker, S
    Sanjurjo, A
    JOURNAL OF CHEMICAL AND ENGINEERING DATA, 2001, 46 (02): : 446 - 450
  • [48] Molecular design of improved precursors for the MOCVD of electroceramic oxides
    Jones, AC
    JOURNAL OF MATERIALS CHEMISTRY, 2002, 12 (09) : 2576 - 2590
  • [49] Selection and design of precursors for the MOCVD of lead scandium tantalate
    Jones, AC
    Davies, HO
    Leedham, TJ
    Crosbie, MJ
    Wright, PJ
    O'Brien, P
    Fleeting, KA
    CHEMICAL PROCESSING OF DIELECTRICS, INSULATORS AND ELECTRONIC CERAMICS, 2000, 606 : 51 - 56
  • [50] Requirements of precursors for MOCVD and ALD of rare earth oxides
    Aspinall, Helen C.
    RARE EARTH OXIDE THIN FILMS: GROWTH, CHARACTERIZATION , AND APPLICATIONS, 2007, 106 : 53 - 72