Comparison of curing depth of a colored polyacid-modified composite resin with different light-curing units

Objective: To compare the depth of cure (DoC) of a colored polyacid-modified composite resin (PAM-C) with a traditional PAM-C and a fine hybrid composite resin using different light-curing units and different radiant energies. Method and Materials: The DoC of the PAM-C Twinky Star (Voco, all shades), the PAM-C Glasiosite (Voco), and the composite resin Z100 (3M ESPE) shades A2 and A4 was determined using a penetrometer test method. The materials were cured in bulk using a halogen-based unit (Elipar Trilight, E = 18 J/cm(2) and E = 32 J/cm(2); 3M ESPE) and an LED curing unit (Elipar Freelight 2, E = 20 J/cm(2); 3M ESPE) in split stainless steel molds. Immediately after curing, the height (mm) of the cured material was measured and taken as the DoC. Ranking of means was performed by Student-Newman-Keuls multiple comparison test, and statistically significant differences among mean values were detected with ANOVA. Results: Mean DoC for all materials and shades varied as follows: 4.705 to 8.870 mm (E = 32 J/cm(2)); 3.672 to 8.050 mm (E = 20 J/cm(2)); and 4.090 to 7.357 mm (E = 18 J/cm(2)). Two-way ANOVA revealed that the DoC depended significantly (P < .001) on the shade of the material and the curing device. Moreover, there was a significant interaction (P < .001) between the latter, indicating that the effect of the energy densities differed quantitatively among the shades. Conclusions: In this study, DoC differed significantly among the materials and the shades. Twinky Star shade blue showed the highest DoC compared to Glasiosite and Z100 shades A2 and A4. The curing device with the highest energy density exhibited the highest curing depths. (Quintessence Int 2010; 41: 787-794)