Stress Oriented Hydrogen Induced Cracking of Linepipe Steel

被引：0

作者：

Kim, Wan Keun ^{[1
]}

Park, Gyu Tae ^{[1
]}

Kim, Kyoo Young ^{[1
]}

机构：

[1] Pohang Univ Sci & Technol, Grad Inst Ferrous Technol, Pohang 790784, South Korea

来源：

JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL | 2011年 / 18卷

关键词：

linepipe steel; stress oriented hydrogen induced cracking; hydrogen induced cracking; metallurgical factor; diffusible hydrogen; LOW-ALLOY STEELS; SOUR ENVIRONMENTS; PIPELINE STEELS; HIGH-STRENGTH; SUSCEPTIBILITY; EMBRITTLEMENT; PERMEATION; MOLYBDENUM; RESISTANCE; IRON;

D O I：

暂无

中图分类号：

TF [冶金工业];

学科分类号：

0806 ;

摘要：

The stress oriented hydrogen induced cracking (SOHIC) is a typical hydrogen embrittlement phenomenon occurring in the linepipe steels exposed to sour environment containing H(2)S gas. However, even recently, the cracking mechanism of SONIC has not been clarified because of lacking in the empirical data on the actual failure mode of SOH IC cracking. The factors affecting SOH IC are discussed in terms of metallurgy of high strength linepipe steel and hydrogen electrochemistry. The cracking mechanisms of SOHIC are examined by comparing them with the empirical failure mode of SOHIC which is developed by observation of the actual fracture sites of the hydrogen induced blister cracking (HIBC) and secondary cracks. Finally, the correlation between SOHIC and HIC is discussed.

引用

页码：121 / 128

页数：8

共 50 条

[21] HYDROGEN INDUCED STRESS CRACKING OF DUPLEX STAINLESS STEEL SUBSEA COMPONENTS
Bahrami, Amir
Woollin, Paul
PROCEEDINGS OF THE ASME 29TH INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, 2010, VOL 6, 2010, : 13 - 22
[22] THE HYDROGEN PERMEATION AND HYDROGEN-INDUCED CRACKING BEHAVIOR OF LINEPIPE IN DYNAMIC FULL SCALE TESTS
HYODO, T
IINO, M
IKEDA, A
KIMURA, M
SHIMIZU, M
CORROSION SCIENCE, 1987, 27 (10-11) : 1077 - 1098
[23] HYDROGEN-INDUCED CRACKING OF LINEPIPE STEELS .1. THRESHOLD HYDROGEN CONCENTRATION AND PH
REVIE, RW
SASTRI, VS
HOEY, GR
RAMSINGH, RR
MAK, DK
SHEHATA, MT
CORROSION, 1993, 49 (01) : 17 - 23
[24] HYDROGEN INDUCED STRESS CRACKING ON SUPERDUPLEX STAINLESS STEEL UNDER CATHODIC PROTECTION
Fonseca, Jose
Renck, Tiago
Abreu, Eliakin
Santos, Fabricio P.
Diehl, Bruno
Fortis Kwietniewski, Carlos E.
33RD INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, 2014, VOL 5, 2014,
[25] Influence of microhardness and inclusion on stress oriented hydrogen induced cracking of line pipe steels
Takahashi, A
Ogawa, H
ISIJ INTERNATIONAL, 1996, 36 (03) : 334 - 340
[26] Relationship between hydrogen-induced additive stress and threshold cracking stress for a pipeline steel
Zhang, Tao
Yao, Yuan
Chu, Wuyang
Qiao, Lijie
Jinshu Xuebao/Acta Metallurgica Sinica, 2002, 38 (08):
[27] Relationship between hydrogen-induced additive stress and threshold cracking stress for a pipeline steel
Zhang, T
Yao, YA
Chu, WY
Qiao, LJ
ACTA METALLURGICA SINICA, 2002, 38 (08) : 844 - 848
[28] Hydrogen induced cracking in high strength steel
Tsuboi, K
Yatabe, H
Yamada, K
MATERIALS SCIENCE AND TECHNOLOGY, 1996, 12 (05) : 400 - 404
[29] HYDROGEN INDUCED DELAYED CRACKING IN MARAGING STEEL
BONISZEW.T
WELDING RESEARCH ABROAD, 1966, 12 (02): : 17 - &
[30] THE EFFECT OF TEST SPECIMEN ORIENTATION ON THE HYDROGEN-INDUCED CRACKING RATING OF LINEPIPE STEEL IN THE NACE TM0284-84 TEST
WENG, YJ
WILDE, BE
MATERIALS PERFORMANCE, 1988, 27 (03) : 31 - 34

← 1 2 3 4 5 →