Perpendicular magnetic anisotropy of Pt/Co2FeAl0.5Si0.5/MgAl2O4 trilayers

被引：17

作者：

Wu, Yong ^{[1
,2
]}

Xu, Xiaoguang ^{[1
]}

Li, Lu ^{[1
]}

Wang, Zhicheng ^{[1
]}

Miao, Jun ^{[1
]}

Jiang, Yong ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, Beijing 100083, Peoples R China

[2] Univ Sci & Technol Beijing, State Key Lab Adv Met, Sch Met & Ecol Engn, Beijing 100083, Peoples R China

来源：

PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE | 2016年 / 213卷 / 10期

基金：

美国国家科学基金会;

关键词：

half-metallic ferromagnet; MgAl2O4; perpendicular magnetic anisotropy; INPLANE; TORQUE;

D O I：

10.1002/pssa.201600160

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Perpendicular magnetic anisotropy ( PMA) has been achieved in Co2FeAl0.5Si0.5 ( CFAS) based trilayers with MgAl2O4 ( MAO) as oxide layer. It was found that the PMA is sensitive to the annealing conditions, the thicknesses of MAO ( t(MAO)) and CFAS ( t(CFAS)) layers. A strong PMA can be observed in the Pt/CFAS/MAO structure after 340 degrees C annealing and maintained as high as 400 degrees C. For a fixed CFAS thickness (t(CFAS) - 1.5 nm), there is a narrow range of tMAO to keep the PMA in this structure. Oxidation at the CFAS/MAO interface plays a very significant role to the PMA, which can be controlled by tuning t(MAO) for fixed annealing temperature and t(CFAS). (C) 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

引用

页码：2780 / 2784

页数：5

共 50 条

[21] Perpendicular magnetic anisotropy in Ta/Pd (0-10 nm)/Co2FeAl0.5Si0.5/MgO/Ta structured films
Fu, H.
You, C.
Zhang, X.
Tian, N.
2015 IEEE MAGNETICS CONFERENCE (INTERMAG), 2015,
[22] Anisotropy and Damping in Co2FeAl0.5Si0.5 via Electrical Detection of Ferromagnetic Resonance
Bai, Lihui
Tezuka, Nobuki
Kohda, Makoto
Nitta, Junsaku
JAPANESE JOURNAL OF APPLIED PHYSICS, 2012, 51 (08)
[23] Interfacial structure and magnetic properties of Co2FeAl0.5Si0.5/MgO heterostructures
Hassan, Sameh S. A.
Xu, Yongbing
Hirohata, Atsufumi
Sukegawa, Hiroaki
Wang, Wenhong
Inomata, Koichiro
van der Laan, Gerrit
JOURNAL OF APPLIED PHYSICS, 2010, 107 (10)
[24] Interlayer exchange coupling in Co2FeAl0.5Si 0.5/Cr/Co2 FeAl0.5Si0.5 trilayers
Furubayashi, T.
Kodama, K.
Goripati, H.S.
Takahashi, Y.K.
Inomata, K.
Hono, K.
Journal of Applied Physics, 2009, 105 (07):
[25] Interaction of Ta-O and perpendicular magnetic anisotropy of Ta/Pd (0-2.4 nm)/Co2FeAl0.5Si0.5/MgO/Ta structured films
You, C. Y.
Fu, H. R.
Zhang, X.
Tian, N.
Wang, P. W.
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2015, 377 : 276 - 280
[26] Insertion layer effects of ultrathin MgAl2O4 oxide on perpendicular magnetic anisotropy properties of Pt/Co2MnSi/MgAl2O4/Pt structures
Wang, Ke
Ling, Wolin
Xu, Zikun
Wu, Liang
Fu, Xiaoyong
MATERIALS SCIENCE AND ENGINEERING B-ADVANCED FUNCTIONAL SOLID-STATE MATERIALS, 2023, 292
[27] Exchange bias induced at a Co2FeAl0.5Si0.5/Cr interface
Yu, C. N. T.
Vick, A. J.
Inami, N.
Ono, K.
Frost, W.
Hirohata, A.
JOURNAL OF PHYSICS D-APPLIED PHYSICS, 2017, 50 (12)
[28] Perpendicular magnetic anisotropy at lattice-matched Co2FeAl/MgAl2O4(001) epitaxial interfaces
Sukegawa, Hiroaki
Hadorn, Jason Paul
Wen, Zhenchao
Ohkubo, Tadakatsu
Mitani, Seiji
Hono, Kazuhiro
APPLIED PHYSICS LETTERS, 2017, 110 (11)
[29] The role of chemical structure on the magnetic and electronic properties of Co2FeAl0.5Si0.5/Si(111) interface
Kuerbanjiang, Balati
Nedelkoski, Zlatko
Kepaptsoglou, Demie
Ghasemi, Arsham
Glover, Stephanie E.
Yamada, Shinya
Saerbeck, Thomas
Ramasse, Quentin M.
Hasnip, Philip J.
Hase, Thomas P. A.
Bell, Gavin R.
Hamaya, Kohei
Hirohata, Atsufumi
Lazarov, Vlado K.
APPLIED PHYSICS LETTERS, 2016, 108 (17)
[30] Interfacial perpendicular magnetic anisotropy in Co2FeSi alloy films sandwiched by Pt and MgAl2O4
Wang, Ke
Xu, Zikun
Yu, Lin
Zhang, Mingzhi
Guo, Xitao
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2022, 560

← 1 2 3 4 5 →