Electrophoretic deposition of CoFe2O4 films from aqueous suspensions

被引：6
|
作者：
Jian, Gang [1 ]
Zhao, Jun [1 ]
Zhou, Dongxiang [1 ]
Fu, Qiuyun [1 ]
机构：
[1] Huazhong Univ Sci & Technol, Dept Elect Sci & Technol, Wuhan 430074, Hubei, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2012年 / 38卷 / 05期
基金：
中国国家自然科学基金;
关键词：
Suspensions; Electrophoretic deposition; CoFe2O4; Preferential orientations; THIN-FILMS; MAGNETIC-PROPERTIES; FOILS;
D O I：
10.1016/j.ceramint.2012.01.014
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
CoFe2O4 nano-particles with average size of similar to 40 nm were synthesized via the chemical coprecipitation method. PAMA-NH4 was used as dispersant to improve the stability of aqueous suspensions. Zeta potential and sediment volumes were tested to study the effects of pH and dispersant amounts on the stability of suspensions. The most stable suspension was obtained when using 0.6 wt.% PAMA-NH4 as dispersant at pH = 10. Conductivity results showed that thoroughly dispersed suspensions were formed after being ultrasonic agitated for 30 min. CoFe2O4 films on Al2O3/Pt substrates fabricated via EPD sintered at 1250 degrees C exhibited preferentially oriented structure. The XRD analyses showed (2 2 0) and (5 1 1) were the preferential orientations. Anisotropy was also observed in magnetic hysteresis loops. Stronger ferromagnetic effect was observed in the in-plane orientation, with saturation magnetization of similar to 290 emu/cm(3). (C) 2012 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：3707 / 3711
页数：5
相关论文
共 50 条
  • [41] Structural, Magnetic and Optical Properties CoFe2O4 Thin Films
    Ravibabu Kancharla
    Ashok Vudayagiri
    Journal of Superconductivity and Novel Magnetism, 2023, 36 : 119 - 130
  • [42] Structural and Magnetic Studies of CoFe2O4 Ferrite, CoFe2O4/CoFe2 Nanocomposites and CoFe2 Nano-alloy
    Ezekiel, I. P.
    Moyo, T.
    Msomi, J. Z.
    Abdallah, H. M. I.
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2017, 30 (08) : 2371 - 2374
  • [43] Comparison XRD pattern of CoFe2O4 thin films and nanoparticles
    Fitriyanti, E.
    Utari
    Purnama, B.
    INTERNATIONAL CONFERENCE ON SCIENCE AND APPLIED SCIENCE 2017, 2017, 909
  • [44] Magnetic properties of ti-doped CoFe2O4 films
    Chae, KP
    Lee, JG
    Kim, WK
    Lee, YB
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2002, 248 (02) : 236 - 240
  • [45] Structural, Magnetic and Optical Properties CoFe2O4 Thin Films
    Kancharla, Ravibabu
    Vudayagiri, Ashok
    JOURNAL OF SUPERCONDUCTIVITY AND NOVEL MAGNETISM, 2023, 36 (01) : 119 - 130
  • [46] Electrochemical synthesis of nanocrystalline CoFe2O4 thin films and their characterization
    Sartale, SD
    Lokhande, CD
    CERAMICS INTERNATIONAL, 2002, 28 (05) : 467 - 477
  • [47] Spin Hall Magnetoresistance in CoFe2O4/Pt Films.
    Wu, H.
    Zhang, Q.
    Wan, C.
    Ali, S.
    You, L.
    Wang, J.
    Choi, Y.
    Han, X.
    2015 IEEE MAGNETICS CONFERENCE (INTERMAG), 2015,
  • [48] Tuning of optical bandgap and magnetization of CoFe2O4 thin films
    Sharma, Deepanshu
    Khare, Neeraj
    APPLIED PHYSICS LETTERS, 2014, 105 (03)
  • [49] CATION DISTRIBUTION IN COFE2O4
    RIECK, GD
    THIJSSEN, JJ
    ACTA CRYSTALLOGRAPHICA SECTION B-STRUCTURAL CRYSTALLOGRAPHY AND CRYSTAL CHEMISTRY, 1968, B 24 : 982 - &
  • [50] Optical and electronic properties of NiFe2O4 and CoFe2O4 thin films
    Rai, R. C.
    Wilser, S.
    Guminiak, M.
    Cai, B.
    Nakarmi, M. L.
    APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING, 2012, 106 (01): : 207 - 211
12345