Encapsulation of Electron Beam Melting Produced Alloy 718 to Reduce Surface Connected Defects by Hot Isostatic Pressing

被引:12
|
作者
Zafer, Yunus Emre [1 ]
Goel, Sneha [1 ]
Ganvir, Ashish [2 ]
Jansson, Anton [3 ]
Joshi, Shrikant [1 ]
机构
[1] Univ West, Dept Engn Sci, S-46186 Trollhattan, Sweden
[2] GKN Aerosp Engine Syst AB, Res & Technol, Dept Proc Engn, S-46181 Trollhattan, Sweden
[3] Orebro Univ, Sch Sci & Engn, S-70182 Orebro, Sweden
关键词
electron beam melting; additive manufacturing; Alloy; 718; surface defects; encapsulation; coating; hot isostatic pressing; SUBSTRATE ROUGHNESS; MICROSTRUCTURAL CHARACTERISTICS; POROSITY; POSTTREATMENTS; ADHESION; BEHAVIOR;
D O I
10.3390/ma13051226
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Defects in electron beam melting (EBM) manufactured Alloy 718 are inevitable to some extent, and are of concern as they can degrade mechanical properties of the material. Therefore, EBM-manufactured Alloy 718 is typically subjected to post-treatment to improve the properties of the as-built material. Although hot isostatic pressing (HIPing) is usually employed to close the defects, it is widely known that HIPing cannot close open-to-surface defects. Therefore, in this work, a hypothesis is formulated that if the surface of the EBM-manufactured specimen is suitably coated to encapsulate the EBM-manufactured specimen, then HIPing can be effective in healing such surface-connected defects. The EBM-manufactured Alloy 718 specimens were coated by high-velocity air fuel (HVAF) spraying using Alloy 718 powder prior to HIPing to evaluate the above approach. X-ray computed tomography (XCT) analysis of the defects in the same coated sample before and after HIPing showed that some of the defects connected to the EBM specimen surface were effectively encapsulated by the coating, as they were closed after HIPing. However, some of these surface-connected defects were retained. The reason for such remnant defects is attributed to the presence of interconnected pathways between the ambient and the original as-built surface of the EBM specimen, as the specimens were not coated on all sides. These pathways were also exaggerated by the high surface roughness of the EBM material and could have provided an additional path for argon infiltration, apart from the uncoated sides, thereby hindering complete densification of the specimen during HIPing.
引用
收藏
页码:1 / 12
页数:12
相关论文
共 50 条
  • [21] Characterization of Spatter and Sublimation in Alloy 718 during Electron Beam Melting
    Raza, Ahmad
    Hryha, Eduard
    MATERIALS, 2021, 14 (20)
  • [22] Effect of hot isostatic pressing on microstructure and mechanical properties of CLAM steel produced by selective laser melting
    Zhai, Yutao
    Huang, Bo
    Mao, Xiaodong
    Zheng, Mingjie
    JOURNAL OF NUCLEAR MATERIALS, 2019, 515 : 111 - 121
  • [23] Hot Isostatic Pressing of Additive Specimens, Grown from IN718 Alloy Powder Obtained by Gas Atomization
    Kasay, P. O.
    Pedash, O. O.
    Klochykhin, V. V.
    Naumyk, V. V.
    Naumyk, O. O.
    STRENGTH OF MATERIALS, 2024, 56 (04) : 722 - 734
  • [24] A Porosity Closure Model Under Hot Isostatic Pressing of an IN718 Alloy Manufactured by Powder Bed Fusion
    Wang, Xuming
    Niu, Liqun
    Cheng, Kaixiong
    Wang, Bingzheng
    Zhang, Qi
    MATERIALS, 2025, 18 (05)
  • [25] Effect of HIPping (Hot Isostatic Pressing) on Electron Beam Melting Ti6Al4V parts after machining
    Dolimont, Adrien
    Michotte, Sebastien
    Riviere-Lorphevre, Edouard
    Ducobu, Francois
    de Formanoir, Charlotte
    Godet, Stephane
    Filippi, Enrico
    PROCEEDINGS OF THE 19TH INTERNATIONAL ESAFORM CONFERENCE ON MATERIAL FORMING (ESAFORM 2016), 2016, 1769
  • [26] Impact of hot isostatic pressing on microstructures of CMSX-4 Ni-base superalloy fabricated by selective electron beam melting
    Ruttert, B.
    Ramsperger, M.
    Roncery, L. Mujica
    Lopez-Galilea, I.
    Koerner, C.
    Theisen, W.
    MATERIALS & DESIGN, 2016, 110 : 720 - 727
  • [27] Effect of Hot Isostatic Pressing on Microstructures and Mechanical Properties of Ti6Al4V Fabricated by Electron Beam Melting
    Liu, Changyong
    Mai, Zhuokeng
    Yan, Deng
    Jiang, Mingguang
    Dai, Yuhong
    Wang, Pei
    Chen, Zhangwei
    Lao, Changshi
    METALS, 2020, 10 (05)
  • [28] Effect of Heat Treatment and Hot Isostatic Pressing on the Corrosion Behavior of Ti6Al4 V Parts Produced by Electron Beam Melting Additive Manufacturing Technology
    Karasoglu, Mutlu
    Oteyaka, Mustafa Ozgur
    Yasa, Evren
    Tan, Evren
    Kushan, Melih Cemal
    ACS OMEGA, 2024, 9 (27): : 29904 - 29916
  • [29] Effects of Hot Isostatic Pressing on Microstructure and Mechanical Properties of Hastelloy X Samples Produced by Selective Laser Melting
    Li, Yali
    Qi, Hai
    Hou, Huipeng
    Lei, Liming
    PROCEEDINGS OF THE SECOND INTERNATIONAL CONFERENCE ON MECHANICS, MATERIALS AND STRUCTURAL ENGINEERING (ICMMSE 2017), 2017, 102 : 31 - 40
  • [30] Effect of hot isostatic pressing on nanoparticles reinforced AlSi10Mg produced by selective laser melting
    Wang, Yachao
    Shi, Jing
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2020, 788