Encapsulation of Electron Beam Melting Produced Alloy 718 to Reduce Surface Connected Defects by Hot Isostatic Pressing

被引:12
|
作者
Zafer, Yunus Emre [1 ]
Goel, Sneha [1 ]
Ganvir, Ashish [2 ]
Jansson, Anton [3 ]
Joshi, Shrikant [1 ]
机构
[1] Univ West, Dept Engn Sci, S-46186 Trollhattan, Sweden
[2] GKN Aerosp Engine Syst AB, Res & Technol, Dept Proc Engn, S-46181 Trollhattan, Sweden
[3] Orebro Univ, Sch Sci & Engn, S-70182 Orebro, Sweden
关键词
electron beam melting; additive manufacturing; Alloy; 718; surface defects; encapsulation; coating; hot isostatic pressing; SUBSTRATE ROUGHNESS; MICROSTRUCTURAL CHARACTERISTICS; POROSITY; POSTTREATMENTS; ADHESION; BEHAVIOR;
D O I
10.3390/ma13051226
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Defects in electron beam melting (EBM) manufactured Alloy 718 are inevitable to some extent, and are of concern as they can degrade mechanical properties of the material. Therefore, EBM-manufactured Alloy 718 is typically subjected to post-treatment to improve the properties of the as-built material. Although hot isostatic pressing (HIPing) is usually employed to close the defects, it is widely known that HIPing cannot close open-to-surface defects. Therefore, in this work, a hypothesis is formulated that if the surface of the EBM-manufactured specimen is suitably coated to encapsulate the EBM-manufactured specimen, then HIPing can be effective in healing such surface-connected defects. The EBM-manufactured Alloy 718 specimens were coated by high-velocity air fuel (HVAF) spraying using Alloy 718 powder prior to HIPing to evaluate the above approach. X-ray computed tomography (XCT) analysis of the defects in the same coated sample before and after HIPing showed that some of the defects connected to the EBM specimen surface were effectively encapsulated by the coating, as they were closed after HIPing. However, some of these surface-connected defects were retained. The reason for such remnant defects is attributed to the presence of interconnected pathways between the ambient and the original as-built surface of the EBM specimen, as the specimens were not coated on all sides. These pathways were also exaggerated by the high surface roughness of the EBM material and could have provided an additional path for argon infiltration, apart from the uncoated sides, thereby hindering complete densification of the specimen during HIPing.
引用
收藏
页码:1 / 12
页数:12
相关论文
共 50 条
  • [1] Hot isostatic pressing of IN718 components manufactured by selective laser melting
    Tillmann, W.
    Schaak, C.
    Nellesen, J.
    Schaper, M.
    Aydinoez, M. E.
    Hoyer, K-P
    ADDITIVE MANUFACTURING, 2017, 13 : 93 - 102
  • [2] Influence of Powder Surface Contamination in the Ni-Based Superalloy Alloy718 Fabricated by Selective Laser Melting and Hot Isostatic Pressing
    Kuo, Yen-Ling
    Kakehi, Koji
    METALS, 2017, 7 (09)
  • [3] The Effectiveness of Hot Isostatic Pressing for Closing Porosity in Titanium Parts Manufactured by Selective Electron Beam Melting
    Samuel Tammas-Williams
    Philip J. Withers
    Iain Todd
    Philip B. Prangnell
    Metallurgical and Materials Transactions A, 2016, 47 : 1939 - 1946
  • [4] The Effectiveness of Hot Isostatic Pressing for Closing Porosity in Titanium Parts Manufactured by Selective Electron Beam Melting
    Tammas-Williams, Samuel
    Withers, Philip J.
    Todd, Iain
    Prangnell, Philip B.
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2016, 47A (05): : 1939 - 1946
  • [5] Electron beam-powder bed fusion of Alloy 718: Effect of hot isostatic pressing and thermal spraying on microstructural characteristics and oxidation performance
    Alehojat, Mobin
    Jafari, Reza
    Karimi, Paria
    Sadeghi, Esmaeil
    SURFACE & COATINGS TECHNOLOGY, 2020, 404
  • [6] Influence of hot isostatic pressing (HIP) on mechanical properties of magnesium alloy produced by selective laser melting (SLM)
    Liu, Shuai
    Guo, Hanjie
    MATERIALS LETTERS, 2020, 265
  • [7] Microstructure and Mechanical Properties of Inconel 718 Powder Alloy Prepared by Hot Isostatic Pressing
    Xu Lei
    Tian Xiaosheng
    Wu Jie
    Lu Zhengguan
    Yang Rui
    ACTA METALLURGICA SINICA, 2023, 59 (05) : 693 - 702
  • [8] Creep and ductility of ODS Cr based alloy produced by hot isostatic pressing
    Buchkremer, HP
    Laptev, AM
    Stover, D
    EUROMAT 97 - PROCEEDINGS OF THE 5TH EUROPEAN CONFERENCE ON ADVANCED MATERIALS AND PROCESSES AND APPLICATIONS: MATERIALS, FUNCTIONALITY & DESIGN, VOL 1, 1997, : 113 - 116
  • [9] Effect of Powder Recycling in Electron Beam Melting on the Surface Chemistry of Alloy 718 Powder
    Gruber, Hans
    Henriksson, Mikael
    Hryha, Eduard
    Nyborg, Lars
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2019, 50A (09): : 4410 - 4422
  • [10] Effect of Powder Recycling in Electron Beam Melting on the Surface Chemistry of Alloy 718 Powder
    Hans Gruber
    Mikael Henriksson
    Eduard Hryha
    Lars Nyborg
    Metallurgical and Materials Transactions A, 2019, 50 : 4410 - 4422