Microstructures and mechanical properties of high performance Mg-4Y-2.4Nd-0.2Zn-0.4Zr alloy

被引：60
|
作者：
Su, Zaijun [1 ]
Liu, Chuming [1 ]
Wan, Yingchun [1 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
MATERIALS & DESIGN | 2013年 / 45卷
关键词：
Y-ND ALLOY; MAGNESIUM ALLOYS; AGING PRECIPITATION; WT.PERCENT ALLOY; MG; ZN; 250-DEGREES-C; EVOLUTION; PHASES;
D O I：
10.1016/j.matdes.2012.07.023
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructures and mechanical properties of the high performance Mg-4Y-2.4Nd-0.2Zn-0.4Zr alloy were investigated. The results showed that the alloy was mainly composed of alpha-Mg, Mg24Y5 and Mg12Nd phases in the as-cast condition. After the solution treatment at 500 degrees C for 6 h and subsequent ageing at different temperatures, alloy exhibited the remarkable mechanical properties. The values of ultimate tensile strength, yield strength and elongation were 339 MPa, 268 MPa and 4.0% in 200 degrees C peak-aged condition, and 330 MPa, 265 MPa and 6.5% in 225 degrees C peak-aged condition, respectively. The high mechanical properties were mainly attributed to a high volume fraction of fine metastable precipitates in the matrix. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：466 / 472
页数：7
相关论文
共 50 条
  • [31] Microstructures and mechanical properties of Mg-Ce-Zn-Zr wrought alloy
    Wen-hua Wu
    Chang-qing Xia
    Journal of Central South University of Technology, 2004, 11 : 367 - 370
  • [32] Dynamic recrystallization behaviors of a Mg-4Y-2Nd-0.2Zn-0.5Zr alloy and the resultant mechanical properties after hot compression
    Zhang, Zhirou
    Yang, Xuyue
    Xiao, Zhenyu
    Wang, Jun
    Zhang, Duxiu
    Liu, Chuming
    Sakai, Taku
    MATERIALS & DESIGN, 2016, 97 : 25 - 32
  • [33] Effect of mold temperature on microstructure and mechanical properties of rheo-squeeze casting Mg-3Nd-0.2Zn-0.4Zr alloy
    Chen, Yushi
    Wu, Guohua
    Liu, Wencai
    Zhang, Liang
    Wang, Quan
    JOURNAL OF MATERIALS RESEARCH, 2017, 32 (22) : 4206 - 4218
  • [34] Evolution of Microstructures, Texture, Damping and Mechanical Properties of Hot Extruded Mg-Nd-Zn-Zr Alloy
    Songhui Wang
    Wencong Zhang
    Jianlei Yang
    Jinqi Pan
    Haixuan Wang
    Wenzhen Chen
    Guorong Cui
    Journal of Materials Engineering and Performance, 2021, 30 : 8872 - 8882
  • [35] Effect of Nd on Microstructure and High-Temperature Mechanical Properties of As-cast Mg-Y-Nd-Zn-Zr Alloy
    Wang, Tao
    Fu, Yuanke
    Wang, Haojie
    Feng, Yicheng
    Guo, Erjun
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2024, 77 (09) : 2857 - 2866
  • [36] Evolution of Microstructures, Texture, Damping and Mechanical Properties of Hot Extruded Mg-Nd-Zn-Zr Alloy
    Wang, Songhui
    Zhang, Wencong
    Yang, Jianlei
    Pan, Jinqi
    Wang, Haixuan
    Chen, Wenzhen
    Cui, Guorong
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2021, 30 (12) : 8872 - 8882
  • [37] Microstructures and mechanical properties of the extruded Mg-4Y-2Gd-xZn-0.4Zr alloys
    Liu, Ke
    Meng, Jian
    JOURNAL OF ALLOYS AND COMPOUNDS, 2011, 509 (07) : 3299 - 3305
  • [38] Effect of Nd and Y addition on microstructure and mechanical properties of extruded Mg-Zn-Zr alloy
    Li, Qiang
    Wang, Qudong
    Li, Daquan
    Ding, Wenjiang
    2006 BIMW: 2006 BEIJING INTERNATIONAL MATERIALS WEEK, PTS 1-4: MAGNESIUM, 2007, 546-549 : 413 - +
  • [39] Effects of minor Y addition on microstructure and mechanical properties of Mg-Nd-Zn-Zr alloy
    Chen, Yushi
    Wu, Guohua
    Liu, Wencai
    Zhang, Liang
    Zhang, Haohao
    Cui, Wendong
    JOURNAL OF MATERIALS RESEARCH, 2017, 32 (19) : 3712 - 3722
  • [40] Effect of Zn concentration on the microstructures and mechanical properties of extruded Mg–7Y–4Gd–0.4Zr alloys
    Ke Liu
    Jinghuai Zhang
    Wei Sun
    Xin Qiu
    Huayi Lu
    Dingxiang Tang
    L. L. Rokhlin
    F. M. Elkin
    Jian Meng
    Journal of Materials Science, 2009, 44 : 74 - 83
12345