Microstructures and mechanical properties of high performance Mg-4Y-2.4Nd-0.2Zn-0.4Zr alloy

被引：60
|
作者：
Su, Zaijun [1 ]
Liu, Chuming [1 ]
Wan, Yingchun [1 ]
机构：
[1] Cent S Univ, Sch Mat Sci & Engn, Changsha 410083, Peoples R China
来源：
MATERIALS & DESIGN | 2013年 / 45卷
关键词：
Y-ND ALLOY; MAGNESIUM ALLOYS; AGING PRECIPITATION; WT.PERCENT ALLOY; MG; ZN; 250-DEGREES-C; EVOLUTION; PHASES;
D O I：
10.1016/j.matdes.2012.07.023
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The microstructures and mechanical properties of the high performance Mg-4Y-2.4Nd-0.2Zn-0.4Zr alloy were investigated. The results showed that the alloy was mainly composed of alpha-Mg, Mg24Y5 and Mg12Nd phases in the as-cast condition. After the solution treatment at 500 degrees C for 6 h and subsequent ageing at different temperatures, alloy exhibited the remarkable mechanical properties. The values of ultimate tensile strength, yield strength and elongation were 339 MPa, 268 MPa and 4.0% in 200 degrees C peak-aged condition, and 330 MPa, 265 MPa and 6.5% in 225 degrees C peak-aged condition, respectively. The high mechanical properties were mainly attributed to a high volume fraction of fine metastable precipitates in the matrix. (C) 2012 Elsevier Ltd. All rights reserved.
引用
收藏
页码：466 / 472
页数：7
相关论文
共 50 条
  • [1] Effect of Y content on microstructure and mechanical properties of Mg-2.4Nd-0.2Zn0.4Zr alloys
    Su, Z. J.
    Liu, C. M.
    Wang, Y. C.
    Shu, X.
    MATERIALS SCIENCE AND TECHNOLOGY, 2013, 29 (02) : 148 - 155
  • [2] Effects of heat treatments on the microstructures and mechanical properties of Mg-3Nd-0.2Zn-0.4Zr (wt.%) alloy
    Fu Penghuai
    Peng Liming
    Jiang Haiyan
    Chang Jianwei
    Zhai Chunquan
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 486 (1-2): : 183 - 192
  • [3] Effects of Homogenizing Treatment on Microstructures and Mechanical Properties of Mg-Nd-Zn-Y-Zr Alloy
    Su Z.
    Jiang H.
    Xiao H.
    Zhongguo Xitu Xuebao/Journal of the Chinese Rare Earth Society, 2020, 38 (06): : 768 - 774
  • [4] Microstructure and Mechanical properties of Extruded Mg-3Nd-0.2Zn-0.4Zr (wt. %) Alloy
    Fu Penghuai
    Peng Liming
    Ma Lan
    Jiang Haiyan
    Zhai Chunquan
    MAGNESIUM TECHNOLOGY 2009, 2009, : 301 - +
  • [5] Microstructure and mechanical properties of Mg-3.0Nd-0.4Zn-0.4Zr magnesium alloy
    Wen, L. H.
    Ji, Z. S.
    Hu, M. L.
    Ning, H. Y.
    JOURNAL OF MAGNESIUM AND ALLOYS, 2014, 2 (01) : 85 - 91
  • [6] Microstructures and mechanical properties of high-strength Mg-Gd-Y-Zn-Zr alloy
    Wang, Zhen-Dong
    Fang, Can-Feng
    Meng, Ling-Gang
    Li, Nai-Pu
    Wu, You-Fang
    Zhang, Xing-Guo
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2012, 22 (01): : 1 - 6
  • [7] Microstructures and mechanical properties of high performance Mg-6Gd-3Y-2Nd-0.4Zr alloy by indirect extrusion and aging treatment
    Liu, Xuan
    Hu, Wenyi
    Le, Qichi
    Zhang, Zhiqiang
    Bao, Lei
    Cui, Jianzhong
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2014, 612 : 380 - 386
  • [8] Effects of pressure and aging treatment on microstructures and mechanical properties of rheo-squeeze casting Mg-3Nd-0.2Zn-0.4Zr alloy
    Chen, Yushi
    Wu, Guohua
    Liu, Wencai
    Zhang, Liang
    Zhang, Song
    JOURNAL OF MATERIALS RESEARCH, 2018, 33 (06) : 758 - 771
  • [9] Microstructures and Mechanical Properties of a Novel Mg-Gd-Y-Zn-Zr Alloy
    Yang, Zhong
    Li, Jianping
    Wang, Yanrong
    Xiong, Biwei
    LIGHT METALS TECHNOLOGY 2013, 2013, 765 : 521 - +
  • [10] Researches on microstructures and mechanical properties of extruded Mg-Zn-Zr-Y alloy
    Peng, Jian
    Liu, Rongshen
    Zhang, Dingfei
    Song, Chengmeng
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 715 - 717
12345