Effect of Thermal Shock and Oxidation on Mechanical Property of Carbon/Carbon Composites with a Silicide Coating

被引：0
|
作者：
Fu Qiangang [1 ]
Li Hejun [1 ]
Li Kezhi [1 ]
Shi Xiaohong [1 ]
Huang Min [1 ]
机构：
[1] NW Polytech Univ, Composites Res Ctr, Lab Ultrahigh Temp Composites, Xian 710072, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2009年 / 38卷
基金：
中国国家自然科学基金;
关键词：
carbon/carbon composites; coating; mechanical properties; CARBON-CARBON COMPOSITES; PROTECTION;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A SiC whisker-toughened MOSi(2)-SiC-Si coating was prepared on carbon/carbon (C/C) composites surface by a two-step technique of slurry and pack cementation, and the effects of thermal shock and oxidation on the mechanical property of the coated C/C were studied. The flexural strength of C/C composites was improved by 6.8% after coated by SiC whisker-toughened MOSi(2)-SiC-Si. After thermal cycle between 1773 K and room temperature in air for 10 times, the mass loss of the coated sample was 5.08% and the percentage of remaining strength was 81.97%. After oxidation at 1773K in air for 60 min, the mass loss of the coated sample was 2.57% and the percentage of remaining strength was 89.63%. The decrease of the flexural strength during the thermal cycle and oxidation tests was primarily due to the oxidation of C/C substrate resulting from the cracking of coating.
引用
收藏
页码：37 / 40
页数：4
相关论文
共 50 条
  • [41] Progress in study of oxidation-resistant and thermal shock-resistant iridium coatings for carbon/carbon composites
    Hua, Yunfeng
    Li, Zhengxian
    Du, Jihong
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (11): : 2059 - 2063
  • [42] Microstructure and Thermal Property of Inert Plasma-Sprayed Tungsten Coating on SiC-Coated Carbon/Carbon Composites
    Wang, Fuqiang
    Chen, Jian
    Cui, Hong
    Ji, Alin
    Xie, Dong
    Zhang, Zhaofu
    FUSION SCIENCE AND TECHNOLOGY, 2022, 78 (03) : 243 - 252
  • [43] Effect of Si/Ta Ratio on the Microstructure and High Temperature Anti-Oxidation Property of SiC/TaSi2 Coating for Carbon/Carbon Composites
    Hou Dangshe
    Li Kezhi
    Li Hejun
    Fu Qiangang
    Zhang Yulei
    Li Xintao
    RARE METAL MATERIALS AND ENGINEERING, 2009, 38 : 252 - 256
  • [44] Microstructure and thermal shock resistance of SiC/CNT-SiC double-layer coating for carbon/carbon composites
    Feng, Lei
    Li, Kezhi
    Si, Zishu
    Li, Hejun
    Song, Qiang
    Shan, Yucai
    Wen, Shiqi
    CERAMICS INTERNATIONAL, 2014, 40 (08) : 13683 - 13689
  • [45] Effect of titania (TiO2) interfacial coating on mechanical properties of carbon-carbon composites
    Dhakate, SR
    Parashar, VK
    Raman, V
    Bahl, OP
    JOURNAL OF MATERIALS SCIENCE LETTERS, 2000, 19 (08) : 699 - 701
  • [46] Experimental investigation of thermal shock effects on carbon-carbon composites
    Leanos, Alma L.
    Prabhakar, Pavana
    COMPOSITE STRUCTURES, 2015, 132 : 372 - 383
  • [47] Computational modeling of carbon/carbon composites under thermal shock conditions
    Leanos, Alma L.
    Prabhakar, Pavana
    COMPOSITE STRUCTURES, 2016, 143 : 103 - 116
  • [48] Effect of CNT orientation on the mechanical property and fracture mechanism of vertically aligned carbon nanotube/carbon composites
    Shen, Sijia
    Yang, Lingwei
    Wang, Chuanyun
    Wei, Liming
    CERAMICS INTERNATIONAL, 2020, 46 (04) : 4933 - 4938
  • [49] Oxidation resistance of a gradient self-healing coating for carbon/carbon composites
    Li, Jun
    Luo, Ruiying
    Lin, Chen
    Bi, Yanhong
    Xiang, Qiao
    CARBON, 2007, 45 (13) : 2471 - 2478
  • [50] IMPROVEMENT OF OXIDATION RESISTANCE OF CARBON/CARBON COMPOSITES BY THE MULTILAYER CVD COATING TECHNIQUE
    SUEMITSU, T
    TAKASHIMA, A
    NISHIKAWA, H
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 1995, 103 (05) : 479 - 483
12345