Effect of Thermal Shock and Oxidation on Mechanical Property of Carbon/Carbon Composites with a Silicide Coating

被引：0
|
作者：
Fu Qiangang [1 ]
Li Hejun [1 ]
Li Kezhi [1 ]
Shi Xiaohong [1 ]
Huang Min [1 ]
机构：
[1] NW Polytech Univ, Composites Res Ctr, Lab Ultrahigh Temp Composites, Xian 710072, Peoples R China
来源：
RARE METAL MATERIALS AND ENGINEERING | 2009年 / 38卷
基金：
中国国家自然科学基金;
关键词：
carbon/carbon composites; coating; mechanical properties; CARBON-CARBON COMPOSITES; PROTECTION;
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
A SiC whisker-toughened MOSi(2)-SiC-Si coating was prepared on carbon/carbon (C/C) composites surface by a two-step technique of slurry and pack cementation, and the effects of thermal shock and oxidation on the mechanical property of the coated C/C were studied. The flexural strength of C/C composites was improved by 6.8% after coated by SiC whisker-toughened MOSi(2)-SiC-Si. After thermal cycle between 1773 K and room temperature in air for 10 times, the mass loss of the coated sample was 5.08% and the percentage of remaining strength was 81.97%. After oxidation at 1773K in air for 60 min, the mass loss of the coated sample was 2.57% and the percentage of remaining strength was 89.63%. The decrease of the flexural strength during the thermal cycle and oxidation tests was primarily due to the oxidation of C/C substrate resulting from the cracking of coating.
引用
收藏
页码：37 / 40
页数：4
相关论文
共 50 条
  • [1] Effect of Thermal Shock and Oxidation on Mechanical Property of Carbon/Carbon Composites with a Silicide Coating
    Fu Qiangang
    稀有金属材料与工程, 2009, 38 (S3) : 37 - 40
  • [2] Effect of Thermal Shock and Oxidation on Mechanical Property of Carbon/Carbon Composites with a Silicide Coating
    Fu Qiangang Li Hejun Li Kezhi Shi Xiaohong Huang Min CC Composites Research Center Laboratory of Ultrahigh Temperature Composites Northwestern Polytechnical University Xian China
    稀有金属材料与工程, 2009, 38(S3) (S3) : 37 - 40
  • [3] Effect of LaB6 on the thermal shock property of MoSi2-SiC coating for carbon/carbon composites
    Li, Ting
    Li, Hejun
    Shi, Xiaohong
    APPLIED SURFACE SCIENCE, 2013, 264 : 88 - 93
  • [4] Mechanical Properties and Thermal Shock Resistance of Rhenium Coating in Iridium/Rhenium/Carbon-Carbon Composites
    Guo Yue
    Xie Hong-yu
    Jiang Zeng-rong
    Xia Zhi-xiang
    2014 ASIA-PACIFIC INTERNATIONAL SYMPOSIUM ON AEROSPACE TECHNOLOGY, APISAT2014, 2015, 99 : 1407 - 1414
  • [5] Effect of pyrocarbon texture on the mechanical and oxidative erosion property of SiC coating for protecting carbon/carbon composites
    Xu, Min
    Guo, Lingjun
    Fu, Yanqin
    CERAMICS INTERNATIONAL, 2021, 47 (23) : 32657 - 32665
  • [6] Thermal Shock Resistance of SiC/Si-Mo Multilayer Oxidation Protective Coating for Carbon/Carbon Silicon Carbide Composites
    Yan, Zhiqiao
    Chen, Feng
    Xiong, Xiang
    Xiao, Peng
    Huang, Baiyun
    JOURNAL OF COMPOSITE MATERIALS, 2010, 44 (26) : 3085 - 3092
  • [7] Effect of isotropic interlayers on the mechanical and thermal properties of carbon/carbon composites
    Zhang, Jincao
    Luo, Ruiying
    Zhang, Yunfeng
    Ni, Yongfeng
    Li, Jinsong
    Yang, Caili
    MATERIALS LETTERS, 2010, 64 (13) : 1536 - 1538
  • [8] Oxidation behavior and thermal-shock resistance of AO20/Si 3 N 4 coating for carbon/carbon composites
    Du, Wenhao
    Zeng, Fanhao
    Dai, Yu
    Gao, Yafang
    Chen, Meiyan
    Li, Zhi
    CERAMICS INTERNATIONAL, 2024, 50 (12) : 21463 - 21472
  • [9] Microstructure and anti-oxidation property of CrSi2-SiC coating for carbon/carbon composites
    Fu, QG
    Li, HJ
    Shi, XH
    Liao, XL
    Li, KZ
    Huang, M
    APPLIED SURFACE SCIENCE, 2006, 252 (10) : 3475 - 3480
  • [10] Preparation and oxidation property of ZrB2-MoSi2/SiC coating on carbon/carbon composites
    Zhang Wu-zhuang
    Zeng Yi
    Gbologah, Lemuel
    Xiong Xiang
    Huang Bai-yun
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2011, 21 (07) : 1538 - 1544
12345