Rapid carbothermic synthesis of silicon carbide nano powders by using microwave heating

This paper reports an improved procedure for synthesis of silicon carbide nanopowders from silica by carbothermic reduction under fast microwave-induced heating. The powders have been prepared by direct solid-state reaction in a 2.45 GHz microwave field in nitrogen atmosphere after 40 h milling. For the first time, the formation of silicon carbide (beta-SiC) as a major phase can be achieved at 1200 degrees C in 5 min of microwave exposure, resulting in nano sized particles ranging from 10 to 40 nm under optimized synthesis condition. The Rietveld quantitative phase-composition analysis confirmed that the major SiC polytype is cubic SiC (beta-SiC) with 98.5(4) weight fraction and the remained is minor hexagonal SiC polytypic (alpha-SiC) phases. Therefore this method is the most efficient one for SiC powder synthesis in terms of energy and time saving as well as preparation of SiC nano powders. (C) 2012 Elsevier Ltd. All rights reserved.