Local analysis of the edge dislocation core in BaTiO3 thin film by STEM-EELS

P>The a < 100 > edge dislocation core formed in an epitaxial BaTiO3 (BTO) thin film grown on a substrate was investigated by scanning transmission electron microscopy combined with electron energy-loss spectroscopy. Elemental analysis using core-loss spectrum indicates that the atomic ratios of O/Ti and Ba/Ti are decreased at the dislocation core. The near-edge fine structure of the oxygen K-edge recorded from the dislocation core differs slightly from that of relaxed BTO region, which suggests that Ba-O bonding is decreased at the dislocation core. The structure of the dislocation core is discussed using a high-angle annular dark-field image and the electron energy-loss spectroscopy results.