Influence of the Compositions of Neutral Soil Media on the Corrosion Cracking of Pipe Steel

被引：12
|
作者：
Voloshyn, V. A. [1 ]
Zvirko, O. I. [1 ]
Sydor, P. Ya. [1 ]
机构：
[1] Ukrainian Natl Acad Sci, Karpenko Physicomech Inst, Lvov, Ukraine
来源：
MATERIALS SCIENCE | 2015年 / 50卷 / 05期
关键词：
soil medium; electrolytes; pipe steel; corrosion cracking; corrosion pits; TRUNK PIPELINE; GAS; DEGRADATION; SERVICE;
D O I：
10.1007/s11003-015-9770-7
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
We study the influence of various electrolytes (chloride, sulfate, carbonate, phosphate, and nitrate ions) on the pitting corrosion resistance and corrosion-cracking resistance characteristics of 17G1S pipe steel in an NS-4 neutral model soil medium. The correlation between these characteristics and possible mechanisms of cracking of pipe steel in the investigated media are analyzed.
引用
收藏
页码：671 / 675
页数：5
相关论文
共 50 条
  • [41] Influence of material and processing on stress corrosion cracking of prestressing steel
    Nurnberger, U
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 1997, 48 (09): : 602 - 612
  • [42] Effect of soil compositions on the electrochemical corrosion behavior of carbon steel in simulated soil solution
    Liu, T. M.
    Wu, Y. H.
    Luo, S. X.
    Sun, C.
    MATERIALWISSENSCHAFT UND WERKSTOFFTECHNIK, 2010, 41 (04) : 228 - 233
  • [43] Stress corrosion cracking of pipeline steel in soil environments of eastern China
    Li, Guangfu
    Huang, Chunbo
    Guo, Hao
    Yang, Wu
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 223 - 226
  • [44] EFFECT OF GRIT BLASTING ON THE STRESS-CORROSION CRACKING BEHAVIOR OF LINE PIPE STEEL
    KOCH, GH
    BARLO, TJ
    BERRY, WE
    MATERIALS PERFORMANCE, 1984, 23 (10) : 20 - 23
  • [45] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    L. I. Nyrkova
    Materials Science, 2020, 56 : 273 - 278
  • [46] Corrosion Cracking of Kh70 Pipe Steel under the Conditions of Cathodic Protection
    Nyrkova, L., I
    MATERIALS SCIENCE, 2020, 56 (02) : 273 - 278
  • [47] Corrosion Behavior of Low Carbon Line Pipe Steel in Soil Environment
    Benmoussat, A.
    Hadjel, M.
    EURASIAN CHEMICO-TECHNOLOGICAL JOURNAL, 2005, 7 (02) : 147 - 156
  • [48] The protective effect of Schiff and Mannich bases on steel corrosion in neutral media
    Altsybeeva, A., I
    Pletnev, M. A.
    Reshetnikov, S. M.
    Shirobokov, I. B.
    INTERNATIONAL JOURNAL OF CORROSION AND SCALE INHIBITION, 2019, 8 (01): : 62 - 68
  • [49] CORROSION INHIBITION OF LOW-CARBON STEEL IN ACID AND NEUTRAL MEDIA
    Plotnikova, M. D.
    Shein, A. B.
    IZVESTIYA VYSSHIKH UCHEBNYKH ZAVEDENII KHIMIYA I KHIMICHESKAYA TEKHNOLOGIYA, 2013, 56 (03): : 35 - +
  • [50] Sodium polyphosphates and silicopolyphosphates as inhibitors of steel corrosion in neutral aqueous media
    Shevchenko, NP
    Ulanova, NM
    Abramova, LI
    Kapralova, VI
    INORGANIC MATERIALS, 1998, 34 (07) : 729 - 732
12345