Microstructure and micro-texture evolution during large strain deformation of aluminium alloy AA 2219

Aluminium alloy AA2219 is widely used in the fabrication of propellant tanks of cryogenic stages of satellite launch vehicles. These propellant tanks are welded structures and a fine grained microstructure is usually preferred for sheets/plates and ring rolled rings used in their fabrication. In order to study the effect of large strain deformation on the microstructural evolution, hot isothermal plane strain compression (PSC) tests were conducted on AA 2219 in the temperature range of 250 degrees C-400 degrees C and at strain rates of 0.01 s(-1) and I s(-1). Flow curves obtained at different temperatures and strain rates exhibited two types of behavior; one with a clear stress peak followed by softening, occurring below Z=2.5E+15 and steady state flow behavior above it. Electron Back-Scatter Diffraction (EBSD) analysis of the PSC tested samples at the location of maximum strain revealed the presence of lamellar microstructures with very low fraction of transverse high angle boundaries (HABs). The loss of HABs during large strain deformation is attributed to the occurrence of dynamic recovery (DRV) as the ratio of calculated to measured lamellar boundary width is less than unity. Based on detailed microstructure and micro texture analysis, it was concluded that it is.very difficult to obtain large fraction of HABs through uniaxial large strain deformation. Therefore, to obtain fine grain microstructure in thermo-mechanically processed AA2219 products, multi-axial deformation is essential. (C) 2016 Elsevier B.V. All rights reserved.