Corrosion behaviour of Zn-Al pseudo-alloy coating on carbon steel in chloride environments

被引：10
|
作者：
Liu An Qiang [1 ]
Xiao Kui [1 ]
Dong Chao Fang [1 ]
Li Xiao Gang [1 ]
机构：
[1] Univ Sci & Technol Beijing, Adv Mat & Technol Inst, Beijing 100083, Peoples R China
来源：
METALLURGY TECHNOLOGY AND MATERIALS | 2012年 / 567卷
关键词：
arc thermal spraying; Zn-Al pseudo-alloy coating; corrosion behavior; salt spray test;
D O I：
10.4028/www.scientific.net/AMR.567.45
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In this work, Zn-Al alloy and Zn-Al pseudo-alloy coatings are deposited on carbon steel by arc spray technology. The corrosion behaviour of the coatings has been studied by salt spray test and electrochemical experiment. The morphology of the coatings exposed to salt spray test for 400 h was analyzed using SEM and EDS. Results show that corrosion rate of Zn-Al alloy coating is faster than that of Zn-Al pseudo-alloy coating and the steel substrate is attacked. The corrosion products formed on the surface of Zn-Al alloy coating were loose, with a large number of cracks and holes, but the Zn-Al pseudo-alloy coating is converted into a stable Al-rich oxide layer, which protects the steel substrate against corrosive attacks and enhances the corrosion resistance of the Zn-Al pseudo-alloy coating. Electrochemical tests show the Zn-Al pseudo-alloy coating as a sacrificial protection coating has the capability of providing sacrificial protection for the steel substrate.
引用
收藏
页码：45 / 48
页数：4
相关论文
共 50 条
  • [31] OXIDATION RESISTANCE OF ZN-AL ALLOY COATED STEEL SHEET
    NUMAKURA, Y
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1985, 71 : 1227 - 1227
  • [32] Effects of Al content on microstructure and corrosion behavior of Zn-Al alloy coatings
    Touane, A.
    Diafi, M.
    Sahnoune, D.
    DIGEST JOURNAL OF NANOMATERIALS AND BIOSTRUCTURES, 2024, 19 (01) : 409 - 416
  • [33] Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates
    Wangping Wu
    Guoqing Sun
    Qinqin Wang
    Sheng Lin
    Journal of Materials Engineering and Performance, 2023, 32 : 10542 - 10555
  • [34] Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates
    Wu, Wangping
    Sun, Guoqing
    Wang, Qinqin
    Lin, Sheng
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (23) : 10542 - 10555
  • [35] Salt spray corrosion and electrochemical corrosion performances of Dacromet fabricated Zn-Al coating
    Liu, Xiaoxiao
    Kong, Dejun
    ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (05) : 565 - 572
  • [36] PROMISING NEW Zn-Al ALLOY QUENCH COATING PROCESS FOR STEEL UNDERGOING PRODUCTION TRIALS.
    Radtke, Schrade F.
    Industrial Heating, 1985, 52 (08): : 37 - 40
  • [37] Influence of Zn-Ni alloy electrodeposition techniques on the coating corrosion behaviour in chloride solution
    Hammami, Olfa
    Dhouibi, Leila
    Triki, Ezzeddine
    SURFACE & COATINGS TECHNOLOGY, 2009, 203 (19): : 2863 - 2870
  • [38] Corrosion behaviour of superplastic Zn-Al alloys in simulated acid rain
    Yang, Lijing
    Zhang, Yangming
    Zeng, Xuduo
    Song, Zhenlun
    CORROSION SCIENCE, 2012, 59 : 229 - 237
  • [39] Zn-Al Anticorrosive Coating Adapted to Obtain Protected Steel Wires
    Tintelecan, Marius
    Ilutiu-Varvara, Dana-Adriana
    Rodriguez Alabanda, Oscar
    Sas-Boca, Ioana-Monica
    Santana Martinez, Gustavo Aristides
    15TH INTERNATIONAL CONFERENCE INTERDISCIPLINARITY IN ENGINEERING, 2022, 386 : 3 - 12
  • [40] MICROSTRUCTURE AND CORROSION BEHAVIOR OF INTERMETALLIC LAYER OF COATING IN ZN-AL ALLOY COATED STEEL WIRE MANUFACTURED BY DOUBLE HOT-DIP PROCESS
    OCHIAI, I
    OHBA, H
    TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1989, 75 (02): : 298 - 305
12345