Crystallization of glasses in the K2O-Nb2O5-SiO2 system

The changes in the structure and phase composition of glasses in the K2O-Nb2O5-SiO2 system upon their heat treatment in the temperature range 700-800degreesC are studied by the small-angle X-ray scattering (SAXS) technique and X-ray powder diffraction. It is demonstrated that the crystallization is the primary process giving rise to microinhomogeneities in glasses due to heat treatment. Nanocrystals of an unidentified niobium-containing phase precipitate in glasses with the formation of regions with a decreased content of potassium and niobium oxides. An increase in the duration of heat treatment at the studied temperatures results in an increase in the size of nanocrystals without change in their phase composition. This is accompanied by the disappearance of diffusion zones, which leads to a decrease in the SAXS intensity in the range of small scattering angles and, correspondingly, to a decrease in the light scattering intensity.