The mechanical properties of W-Cu composite by activated sintering

被引：55

作者：

Chen, Pingan ^{[1
]}

Shen, Qiang ^{[1
]}

Luo, Guoqiang ^{[1
]}

Li, Meijuan ^{[1
]}

Zhang, Lianmeng ^{[1
]}

机构：

[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2013年 / 36卷

关键词：

W-Cu composites; Sintering; Diffusion; Mechanical properties; TRANSVERSE RUPTURE STRENGTH; DENSIFICATION; TUNGSTEN; CONDUCTIVITY; BEHAVIOR; SIZE; CO;

D O I：

10.1016/j.ijrmhm.2012.09.001

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The effects of Zn additive and processing parameters on bending strength and hardness of W-Cu composite, which is fabricated at very low temperature by powder metallurgy, have been investigated. The bending strength and hardness increase with Zn additive content increasing and processing parameter optimization. When the Zn additive content is 14 wt.%, the bending strength of W-Cu composite reaches its maximum value (960 MPa), which is almost two times higher than the one without any additive. From fractographs of W-Cu composite, the intragranular fracture of W particles and ductility of Cu matrix indicate that proper Zn additive content and optimal processing parameters make the presence of strong grain-boundaries and lead to a higher measured bending strength and hardness. Therefore, Zn additive plays a key role in increasing the bending strength and hardness of W-Cu composite at the condition of optimal processing parameters. (C) 2012 Published by Elsevier Ltd.

引用

页码：220 / 224

页数：5

共 50 条

[41] The densification of W-Cu green in continuous liquid phase sintering
Shanghai University, Shanghai 200072, China
Xiyou Jinshu Cailiao Yu Gongcheng, 2009, 4 (730-733):
[42] Properties of W-Cu composite powders synthesized by sol-ball milling
Fan, Jing-Lian
Guo, Yao-Feng
Jiang, Dong-Fu
Liu, Tao
Fan, J.-L., 1600, Journal of Functional Materials, P.O. Box 1512, Chongqing, 630700, China (44): : 2927 - 2930
[43] SINTERING OF W-CU CONTACT MATERIALS WITH NI AND CO DOPANTS
MOON, IH
LEE, JS
POWDER METALLURGY INTERNATIONAL, 1977, 9 (01): : 23 - 24
[44] Formation of a novel W-rim/Cu-core structure during direct laser sintering of W-Cu composite system
Gu, Dongdong
Shen, Yifu
Wu, Xiajuan
MATERIALS LETTERS, 2008, 62 (12-13) : 1765 - 1768
[45] Apparent viscosity of W-Cu powder compacts during sintering
Doré, F
Martin, CL
Allibert, CH
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2004, 383 (02): : 390 - 398
[46] Phase stability and mechanical property of W-Cu solid solutions from a newly derived W-Cu potential
Yang, Lingyun
Shen, Yuanjun
Mi, Shiteng
Fan, Jinglian
Gong, Haoran
PHYSICA B-CONDENSED MATTER, 2022, 624
[47] Microstructural studies of W-Cu nanostructured precursor composite powders prepared by mechanical alloying
Zhu, Y. B.
Shen, Y. F.
Gu, D. D.
Wu, P.
Huang, Z.
POWDER METALLURGY, 2007, 50 (03) : 223 - 227
[48] Fabrication of W-Cu nano-crystalline composite precursor powders by mechanical alloying
Zhu Yongbing
Shen Yifu
RARE METAL MATERIALS AND ENGINEERING, 2007, 36 (06) : 1091 - 1094
[49] Effects of Cu content and mechanical alloying parameters on the preparation of W-Cu composite coatings on copper substrate
Meng, Yunfei
Shen, Yifu
Chen, Cheng
Li, Yongcan
Feng, Xiaomei
JOURNAL OF ALLOYS AND COMPOUNDS, 2014, 585 : 368 - 375
[50] Compact and mechanical properties of W-Cu gradient heat-sink materials
Liu Binbin
Lu Yannan
Xie Jianxin
RARE METAL MATERIALS AND ENGINEERING, 2008, 37 (04) : 697 - 700

← 1 2 3 4 5 →