The mechanical properties of W-Cu composite by activated sintering

被引：55
|
作者：
Chen, Pingan [1 ]
Shen, Qiang [1 ]
Luo, Guoqiang [1 ]
Li, Meijuan [1 ]
Zhang, Lianmeng [1 ]
机构：
[1] Wuhan Univ Technol, State Key Lab Adv Technol Mat Synth & Proc, Wuhan 430070, Peoples R China
来源：
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2013年 / 36卷
关键词：
W-Cu composites; Sintering; Diffusion; Mechanical properties; TRANSVERSE RUPTURE STRENGTH; DENSIFICATION; TUNGSTEN; CONDUCTIVITY; BEHAVIOR; SIZE; CO;
D O I：
10.1016/j.ijrmhm.2012.09.001
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The effects of Zn additive and processing parameters on bending strength and hardness of W-Cu composite, which is fabricated at very low temperature by powder metallurgy, have been investigated. The bending strength and hardness increase with Zn additive content increasing and processing parameter optimization. When the Zn additive content is 14 wt.%, the bending strength of W-Cu composite reaches its maximum value (960 MPa), which is almost two times higher than the one without any additive. From fractographs of W-Cu composite, the intragranular fracture of W particles and ductility of Cu matrix indicate that proper Zn additive content and optimal processing parameters make the presence of strong grain-boundaries and lead to a higher measured bending strength and hardness. Therefore, Zn additive plays a key role in increasing the bending strength and hardness of W-Cu composite at the condition of optimal processing parameters. (C) 2012 Published by Elsevier Ltd.
引用
收藏
页码：220 / 224
页数：5
相关论文
共 50 条
  • [1] Thermal and electrical properties of W-Cu composite produced by activated sintering
    Chen, Pingan
    Luo, Guoqiang
    Shen, Qiang
    Li, Meijuan
    Zhang, Lianmeng
    MATERIALS & DESIGN, 2013, 46 : 101 - 105
  • [2] Activated sintering of premixed and coated W-Cu alloys
    Ghosh, C
    Upadhyaya, A
    TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS, 2002, 55 (06): : 535 - 542
  • [3] The activated sintering of W-Cu composites through spark plasma sintering
    Luo, Chunlan
    Wang, Yan
    Xu, Juexin
    Xu, Gaoyong
    Yan, Zizhi
    Li, Jingzhi
    Li, Hui
    Lu, Hui
    Suo, Jinping
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2019, 81 : 27 - 35
  • [4] Activated liquid phase sintering of W-Cu and Mo-Cu
    Johnson, John L.
    INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2015, 53 : 80 - 86
  • [5] Nanostructural characteristics and sintering behavior of W-Cu composite powder prepared by mechanical alloying
    Department of Materials Engineering, Hanyang University, Seoul, Korea, Republic of
    J Adv Mater, 4 (37-44):
  • [6] Nanostructural characteristics and sintering behavior of W-Cu composite powder prepared by mechanical alloying
    Kim, JC
    Ryu, SS
    Moon, IH
    JOURNAL OF ADVANCED MATERIALS, 1999, 31 (04): : 37 - 44
  • [7] Spark plasma sintering on mechanically activated W-Cu powders
    Jia, CC
    Li, ZG
    He, YT
    Qu, XH
    RARE METALS, 2004, 23 (03) : 269 - 273
  • [8] Spark plasma sintering on mechanically activated W-Cu powders
    JIA Chengchang
    Rare Metals, 2004, (03) : 269 - 273
  • [9] Vacuum diffusion bonding W to W-Cu composite: Interfacial microstructure and mechanical properties
    Yan, Haixiang
    Fan, Jinglian
    Han, Yong
    Yao, Qing
    Liu, Tao
    Lv, Yongqi
    Zhang, Chenggong
    VACUUM, 2019, 165 : 19 - 25
  • [10] Effect of Mechanical Activation Time on the Structure and Mechanical Properties of W-Cu Powder Composite
    Evstratov, E. V.
    Baikin, A. S.
    Averin, S. I.
    INORGANIC MATERIALS-APPLIED RESEARCH, 2023, 14 (5-6) : 1408 - 1413
12345