Synthesis and microstructural evolution of nanocrystalline Al-Fe-V-Si-Nd alloy powder

被引：0
|
作者：
Zheng, LJ [1 ]
Zeng, MG [1 ]
Lin, JX [1 ]
机构：
[1] Northeastern Univ, Dept Mat Sci, Shenyang 110006, Peoples R China
来源：
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA | 2001年 / 11卷 / 06期
关键词：
rare earth Nd; mechanical alloying; Al-Fe-V-Si-Nd alloy; alpha (Al) nanocrystalline; alpha-Al-13(Fe; V)(3)Si phase;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The nanocrystallic Al93.3-xFe4.3V0.7Si1.7Nd.(x = 0, 1.0, 3.0) alloy powder was fabricated by mechanical alloying, and the microstructural evolution of alloy powder during mechanical alloying and annealing treatment were studied. It was found that under the condition of vibration ball-milling for 96 h, the microstructure of Al93.3 - xFe4.3V0.7Si1.7Ndx, alloy powder still consisted of single a (Al) solid solution phase without the trace of presence of intermetalic compound; after the appropriate heat treatment, the microstructure of Al93.3-xFe4.3V0.7Ndx alloy powder consisted mainly of nanocrystalline alpha (Al) phase and alpha -Al-13 (Fe, V)(3) Si phase; the addition of rare earth Nd enhanced the grain refining and amorphous inclination of Al solid solution during mechanical alloying, and resulted in new phases formed after heat treatment.
引用
收藏
页码：923 / 926
页数：4
相关论文
共 50 条
  • [41] Synthesis and Characterization of Nanocrystalline Ni-Cr-Al Alloy Powder
    Singh, Daljeet
    Kumar, Rajiv
    MATERIALS TODAY-PROCEEDINGS, 2021, 41 : 821 - 824
  • [42] Al-V合金预磨状态对Al-Fe-V-Si-Nd机械合金化过程中显微组织演化的影响
    郑立静
    曾梅光
    贾威
    中国有色金属学报, 2000, (S1) : 218 - 219
  • [43] Microstructural characterization of atomized powder of Al-5Mn-5Fe-2Si (wt.%) alloy
    Bendersky, L.A.
    Biancaniello, F.S.
    Ridder, S.D.
    Shapiro, A.J.
    Materials Science and Engineering A, 1991, A134 : 1098 - 1102
  • [44] Microstructural and Magnetic Behavior of Nanocrystalline Fe-12Ni-16B-2Si Alloy Synthesis and Characterization
    Zaara, Kaouther
    Khitouni, Mohamed
    Escoda, Lluisa
    Saurina, Joan
    Sunol, Joan-Josep
    Llorca-Isern, Nuria
    Chemingui, Mahmoud
    METALS, 2021, 11 (11)
  • [45] Microstructural Refinement and α-Dispersoid Evolution in Direct-Chill Cast Al-Mg-Si-Fe Alloy
    Wang, Dongtao
    Zhang, Haitao
    Nagaumi, Hiromi
    Li, Xueke
    Cui, Jianzhong
    ADVANCED ENGINEERING MATERIALS, 2020, 22 (12)
  • [46] Microstructural evolution of Al-20Si-5Fe alloy during rapid solidification and hot consolidation
    M.Rajabi
    M.Vahidi
    A.Simchi
    P.Davami
    RareMetals, 2009, 28 (06) : 639 - 645
  • [47] Microstructural evolution of Al-20Si-5Fe alloy during rapid solidification and hot consolidation
    M. Rajabi
    M. Vahidi
    A. Simchi
    P. Davami
    Rare Metals, 2009, 28 : 639 - 645
  • [48] Microstructural evolution of Al-20Si-5Fe alloy during rapid solidification and hot consolidation
    Rajabi, M.
    Vahidi, M.
    Simchi, A.
    Davami, P.
    RARE METALS, 2009, 28 (06) : 639 - 645
  • [49] MICROSTRUCTURAL DEVELOPMENT DURING CONSOLIDATION OF RAPIDLY SOLIDIFIED AL-FE-V-SI POWDER BY VHP, EXTRUSION AND ROLLING
    WANG, Y
    LORIMER, GW
    SALE, FR
    SCRIPTA METALLURGICA ET MATERIALIA, 1994, 31 (10): : 1337 - 1342
  • [50] HOT EXTRUSION PROCESS FOR FE-SI-AL ALLOY POWDER
    不详
    TRANSACTIONS OF THE IRON AND STEEL INSTITUTE OF JAPAN, 1988, 28 (05) : 416 - 416
12345