Phase relation of Sm-Fe-V alloys around the compound Sm-3(Fe,V)(29)

被引：18
|
作者：
Sugimoto, S
Shimono, T
Nakamura, H
Kagotani, T
Okada, M
Homma, M
机构：
[1] Department of Materials Science, Faculty of Engineering, Tohoku University
来源：
MATERIALS TRANSACTIONS JIM | 1996年 / 37卷 / 03期
关键词：
phase relation; Sm-3(Fe; V)(29); compound; isothermal section; microstructure; annealing; X-ray diffraction; SEM-EDX;
D O I：
10.2320/matertrans1989.37.494
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Phase relations in the Sm-Fe-V system, especially around the compound Sm-3(Fe,V)(29), have been studied. Isothermal sections of the iron-rich corner of the Sm-Fe-V system were constructed from X-ray diffraction studies and microstructural observations. alpha-(Fe,V), gamma-(Fe,V), Sm-2(Fe,V)(17), Sm(Fe,V)(12) and liquid phases are present near the Sm-3(Fe,V)(29) compound after annealing at 1100 degrees C. However, nearly single phase Sm-3(Fe,V)(29) can be obtained with an alloy of composition Sm9.5Fe83.5V7. The solid solubility of Sm in Sm-3(Fe,V)29 compound is very small, but that of V is in the range 5.6 at% to 9.2 at%. The liquid phase region expands to the lower V content with increasing annealing temperature, leading to a decreasing V content in the Sm(Fe,V)(12) compound at high temperature.
引用
收藏
页码：494 / 498
页数：5
相关论文
共 50 条
  • [31] Fe-Sm-V (iron-samarium-vanadium)
    Raghavan, V
    JOURNAL OF PHASE EQUILIBRIA, 2001, 22 (05): : 575 - 576
  • [32] Effect of Co on twin formation and magnetic properties of Sm(Fe,Ti, V)12 alloys
    Tozman, P.
    Hrkac, G.
    Patrick, C. E.
    Staunton, J. B.
    Saito, T.
    Sasaki, T.
    Ohkubo, T.
    Sepehri-Amin, H.
    SCRIPTA MATERIALIA, 2025, 258
  • [33] Magnetocrystalline anisotropy and exchange interactions in novel compounds R(3)(Fe,V)(29) (R=Y, Nd, Sm)
    Shcherbakova, YV
    Ivanova, GV
    Bartashevich, MI
    Khrabrov, VI
    Belozerov, YV
    FIZIKA METALLOV I METALLOVEDENIE, 1996, 81 (04): : 96 - 104
  • [34] Magnetocrystalline anisotropy and exchange interactions in the novel R(3)(Fe,V)(29) compounds (R=Y, Nd, Sm)
    Shcherbakova, YV
    Ivanova, GV
    Bartashevich, MI
    Khrabrov, VI
    Belozerov, YV
    JOURNAL OF ALLOYS AND COMPOUNDS, 1996, 240 (1-2) : 101 - 106
  • [35] Peculiarities of the R-3(Fe,Si)(29) phase formation in the Sm-Fe-Si system
    Ivanova, GV
    Makarova, GM
    Shcherbakova, YV
    Belozerov, YV
    Yermolenko, AS
    JOURNAL OF ALLOYS AND COMPOUNDS, 1997, 260 (1-2) : 139 - 142
  • [36] Mechanism of the Y2(Fe, V)17 → Y3(Fe, V)29 phase transformation
    Ivanova, GV
    Makarova, GM
    Shcherbakova, EV
    Teitel, EI
    PHYSICS OF METALS AND METALLOGRAPHY, 2000, 89 (05): : 501 - 507
  • [37] Preparation SM2Fe17 Alloys in Ca-SM2O3-Fe system
    Deng, GF
    Sun, GF
    Chen, JF
    Qi, YJ
    Pan, LJ
    Fang, KM
    JOURNAL OF RARE EARTHS, 2005, 23 (05) : 530 - 533
  • [38] Phase relations of the Sm-Fe-Ti system around the compound SmFe11Ti
    Kim, Yoon-Bae
    Sugimoto, Satoshi
    Okada, Masuo
    Homma, Motofumi
    1600, (176):
  • [39] Preparation of Sm2Fe17Alloys in Ca-Sm2O3-Fe System
    邓庚凤
    孙光飞
    陈菊芳
    祁毓俊
    庞利佳
    方克明
    JournalofRareEarths, 2005, (05) : 530 - 533
  • [40] Phase equilibria in iron-rich Sm–Fe–Ti and Sm–(Fe,Co)–Ti alloys at 1100–1200 °C
    Department of Physics and Astronomy, University of Delaware, Newark
    DE
    19716, United States
    不详
    DE
    19716, United States
    不详
    MA
    02115, United States
    J Alloys Compd, 2023,
12345