Surface Profile Observation of PTFE Radial Bearings under Rolling-Contact-Fatigue in Water

被引：1
|
作者：
Oyama, Shunsuke [1 ]
Kida, Katsuyuki [1 ]
Santos, Edson Costa [1 ]
Koike, Hitonobu [1 ]
Kashima, Yuji [2 ]
机构：
[1] Kyushu Univ, Dept Mech Eng, Nishi Ku, 744 Motooka, Fukuoka 812, Japan
[2] Kashima Plast Bearings Corp, Nishiyodogawa Ku, Osaka, Japan
来源：
MECHATRONICS AND COMPUTATIONAL MECHANICS | 2013年 / 307卷
关键词：
Tribology; Rolling Contact fatigue; Polymer Bearing; PTFE; Wear; POLYMER BEARINGS; ROTATION SPEED; PEEK BEARINGS; LOAD; RACE;
D O I：
10.4028/www.scientific.net/AMM.307.337
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Groove shape effect on wear behavior in PTFE radial bearings under rolling contact fatigue (RCF) was investigated. RCF tests in water-lubricated conditions were carried out at different loads and rotation speeds. The groove surfaces after testing were observed by using a laser confocal microscope and a two-dimensional shape measurement sensor. It was found that PTFE bearings under RCF generate wear debris, however no cracking or flaking failure could be observed. It is concluded that groove deformation depend on load rather than rotation speed. The biggest changes in groove profiles occurred when tested at loads close to 400N.
引用
收藏
页码：337 / +
页数：2
相关论文
共 50 条
  • [1] Surface Profile Observation of PTFE Thrust Bearings under Rolling Contact Fatigue in Water
    Itakura, Kiyoto
    Honda, Takashi
    Oyama, Shunsuke
    Kida, Katsuyuki
    Hazeyama, Shintaro
    Kashima, Yuji
    ADVANCED MATERIALS AND ENGINEERING MATERIALS II, 2013, 683 : 391 - +
  • [2] Comparison of wear on PEEK-PTFE and PPS-PTFE radial bearings under Rolling Contact Fatigue
    Koike, Hitonobu
    Mizobe, Koshiro
    Oyama, Shunsuke
    Kashima, Yuji
    Kanemasu, Kenji
    Kida, Katsuyuki
    ADVANCED MATERIALS DESIGN AND MECHANICS II, 2013, 372 : 503 - +
  • [3] Surface crack and wear of PPS polymer thrust bearings under rolling contact fatigue in water
    Shi, X.
    Kida, K.
    Kashima, Y.
    MATERIALS RESEARCH INNOVATIONS, 2014, 18 : 42 - 47
  • [4] Influence of groove shape on rolling contact fatigue of PEEK-PTFE hybrid radial bearings in dry conditions
    Inagaki, Masahiro
    Mizobe, Koshiro
    Kida, Katsuyuki
    Kashima, Yuji
    2ND INTERNATIONAL CONFERENCE ON COMPOSITE MATERIAL, POLYMER SCIENCE AND ENGINEERING (CMPSE2018), 2019, 264
  • [5] Surface crack growth of silicon nitride bearings under rolling contact fatigue
    Kida, K
    Urakami, T
    Yamazaki, T
    Kitamura, K
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (08) : 657 - 668
  • [6] The Influence of Surface Texture on Rolling-Contact Fatigue of PEEK Bearings in Water
    Honda, Takashi
    Kida, Katsuyuki
    Santos, Edson Costa
    Kashima, Yuji
    MATERIALS PROCESSING TECHNOLOGIES, PTS 1 AND 2, 2011, 154-155 : 1713 - +
  • [7] Self-lubrication of PEEK polymer bearings in rolling contact fatigue under radial loads
    Koike, H.
    Kida, K.
    Santos, E. C.
    Rozwadowska, J.
    Kashima, Y.
    Kanemasu, K.
    TRIBOLOGY INTERNATIONAL, 2012, 49 : 30 - 38
  • [8] Crack initiation from micro surface holes in bearings under rolling contact fatigue
    Kida, K
    Yamazaki, T
    Shibata, M
    Oguma, N
    Harada, H
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2004, 27 (06) : 481 - 493
  • [9] Rolling-contact-fatigue and wear of rails: Economic and technical aspects
    Pointner, P
    SYSTEM DYNAMIC AND LONG-TERM BEHAVIOUR OF RAILWAY VEHICLES,TRACK AND SUBGRADE, 2003, 6 : 51 - 62
  • [10] Wear of hybrid radial bearings (PEEK ring-PTFE retainer and alumina balls) under dry rolling contact
    Koike, Hitonobu
    Kida, Katsuyuki
    Mizobe, Koshiro
    Shi, Xiaochen
    Oyama, Shunsuke
    Kashima, Yuji
    TRIBOLOGY INTERNATIONAL, 2015, 90 : 77 - 83
12345