Photoluminescence properties of ZnSe/SiO2 composite thin films prepared by sol-gel method

ZnSe/SiO2 composite thin films was prepared by sol-gel method. XRD results indicate the phase structure of ZnSe particles embedded in ZnSe/SiO2 composite thin films is sphalerite (cubic ZnS). Spectroscopic ellipsometers were used to investigated the dependences of ellipsometric angle with wavelength of ZnSe/SiO2 composite thin films. The optical constant, thickness, porosity and the concentration of ZnSe of ZnSe/SiO2 thin composite films were fitted according to Maxwell-Gamett effective medium theory The thickness of ZnSe/SiO2 composite thin thin films was also measured through surface profile. The photoluminescence properties of ZnSe/SiO2 thin composite thin films was investigated through fluorescence spectrometer. The photoluminescence results show that the emission peak at 487 run (2.5 eV) is excited at 395 nm corresponds to the hand-to-hand emission of sphalerite ZnSe crystal(2.58 eV). The strength free exciton emission and other emission peaks correlating to ZnSe lattice defect were also observed.