TEM investigation of intergranular stress corrosion cracking for 316 stainless steel in PWR environment

被引：38
|
作者：
Huang, YZ [1 ]
Titchmarsh, JM [1 ]
机构：
[1] Univ Oxford, Dept Mat, Oxford OX1 3PH, England
来源：
ACTA MATERIALIA | 2006年 / 54卷 / 03期
关键词：
stainless steel; stress corrosion cracking; crack tip; grain boundary; transmission electron microscopy;
D O I：
10.1016/j.actamat.2005.10.011
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Type 316 stainless steel foils containing stress corrosion cracks grown in high temperature aqueous environments have been examined by transmission electron microscopy. It was found that the crack tips are oxidized and have a three-layered morphology where all the layers taper towards the crack tip. The inner layer is a microcrystalline spinel sandwiched between the outer layers of a nano-crystalline oxide. The outer layers are enriched in Cr, and the inner with Fe, relative to the matrix. Cu was observed to segregate at the interface between oxide and matrix at one crack in type 316 steel. The inner oxide growth is dominated by different mechanisms before and after the grain boundary cracks. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：635 / 641
页数：7
相关论文
共 50 条
  • [21] Investigation of intergranular stress corrosion cracking in a failed 347H stainless steel furnace tube
    Mahalli, Milad Shabani
    Ahmadi, Azin
    Sabouri, Mohsen
    ENGINEERING FAILURE ANALYSIS, 2022, 142
  • [22] On the mechanism of intergranular stress corrosion cracking of sensitized stainless steel in tetrathionate solution
    Yonezu, Akio
    Kusano, Ryota
    Chen, Xi
    JOURNAL OF MATERIALS SCIENCE, 2013, 48 (06) : 2447 - 2453
  • [23] A micromechanical analysis of intergranular stress corrosion cracking of an irradiated austenitic stainless steel
    Liang, D.
    Hure, J.
    Courcelle, A.
    El Shawish, S.
    Tanguy, B.
    ACTA MATERIALIA, 2021, 204
  • [24] Ultrasonic characterization of intergranular stress corrosion cracking in austenitic stainless steel welds
    Bandyopadhyay, M
    Nanekar, PP
    Shah, BK
    Ramanathan, R
    Mangsulikar, MD
    Kulkarni, PG
    TRENDS IN NDE SCIENCE AND TECHNOLOGY - PROCEEDINGS OF THE 14TH WORLD CONFERENCE ON NDT (14TH WCNDT), VOLS 1-5, 1996, : 2197 - 2200
  • [25] Mechanical criterion for nucleation of intergranular stress corrosion cracking in austenitic stainless steel
    Fujii, Tomoyuki
    Sawada, Tatsuro
    Tohgo, Keiichiro
    Shimamura, Yoshinobu
    FORCES IN MECHANICS, 2021, 3
  • [26] Detection and characterisation of intergranular stress-corrosion cracking on austenitic stainless steel
    Kovac, J.
    Marrow, T. J.
    Govekar, E.
    Legat, A.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2012, 63 (08): : 664 - 673
  • [27] On the mechanism of intergranular stress corrosion cracking of sensitized stainless steel in tetrathionate solution
    Akio Yonezu
    Ryota Kusano
    Xi Chen
    Journal of Materials Science, 2013, 48 : 2447 - 2453
  • [28] STRESS-CORROSION CRACKING SUSCEPTIBILITY OF AISI-316-NG AND 316 STAINLESS-STEEL IN AN IMPURITY ENVIRONMENT
    MAIYA, PS
    SHACK, WJ
    CORROSION, 1985, 41 (11) : 630 - 634
  • [29] An investigation of alloy 182 stress corrosion cracking in simulated PWR environment
    Bamford, WH
    Foster, JP
    Pathania, RS
    PROCEEDINGS OF THE NINTH INTERNATIONAL SYMPOSIUM ON ENVIRONMENTAL DEGRADATION OF MATERIALS IN NUCLEAR POWER SYSTEMS-WATER REACTORS, 1999, : 279 - 282
  • [30] Microstructural characterization on intergranular stress corrosion cracking of Alloy 600 in PWR primary water environment
    Lim, Yun Soo
    Kim, Hong Pyo
    Hwang, Seong Sik
    JOURNAL OF NUCLEAR MATERIALS, 2013, 440 (1-3) : 46 - 54
12345