Density changes in amorphous silicon induced by swift heavy ions

Pure and gold-doped amorphous silicon membranes were irradiated with swift heavy ions (75 MeV Ag or 1.1 GeV Au ions) and studied using small-angle x-ray scattering. The samples that were irradiated with 1.1 GeV Au ions produced a scattering pattern consistent with core-shell-type ion tracks of 2.0 +/- 0.1 nm (core) and 7.0 +/- 0.3 nm (total) radius irrespective of gold doping, consistent with radii previously observed [9]. The density in the core is nearly 4% different from that of the surrounding material. The entire track (core + shell) is slightly less dense than the surrounding material, yielding an expansion or hammering constant A of 0.036 +/- 0.003 nm2 per ion track, consistent with the macroscopic "hammering" deformation. No tracks were found in samples irradiated with 75 MeV Ag ions, and no signature specific to the gold impurity doping could be observed.