Tension-Tension Fatigue Behaviour of Carbon Nanotube Reinforced Aluminium Composites

被引:11
|
作者
Liao, Jinzhi [1 ]
Tan, Ming-Jen [1 ]
Emin, Bayraktar [2 ]
机构
[1] Nanyang Technol Univ, Sch Mech & Aerosp Engn, 50 Nanyang Ave, Singapore 639798, Singapore
[2] Supermeca LISMMA, Sch Mech & Manufacturing Engn, F-94307 Paris, France
来源
关键词
Aluminium composite; Carbon nanotubes; Fatigue; Cyclic softening; Dislocation rearrangement; MATRIX; EVOLUTION;
D O I
10.4028/www.scientific.net/MSF.765.563
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
Fatigue characterization is an important concern for structural materials. The fatigue behaviour of aluminium (Al) composite reinforced with carbon nanotubes (CNT) is of interest besides its improved strength. In this study, tension-tension fatigue tests were conducted on monolithic Al and Al reinforced with 0.5, 1 and 2 weight percentages of CNT. Experimental results showed that the addition of CNTs significantly increased the number of load cycles to failure for each loading case. CNTs could slow fatigue crack propagation by crack-bridging and CNT frictional pull-out mechanisms. Cyclic softening was observed for both monolithic Al and Al-0.5CNT fatigued at an intermediate-high maximum stress of 120 MPa. TEM studies showed that the cyclic softening was attributed to the rearrangement of dislocations into lower potential energy configurations, i.e. parallel arrays and twin boundary dislocations.
引用
收藏
页码:563 / +
页数:2
相关论文
共 50 条
  • [31] Modeling damage and load redistribution in composites under tension-tension fatigue loading
    Kassapoglou, Christos
    Kaminski, Myriam
    COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2011, 42 (11) : 1783 - 1792
  • [32] BIAXIAL TENSION-TENSION FATIGUE STRENGTHS OF METALS
    MARIN, J
    JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME, 1949, 16 (04): : 383 - 388
  • [33] Considerations on Tension-Tension Fatigue Predictions for Nitinol
    Launey, Maximilien E.
    Ong, Ich
    Berg, Brian T.
    Pelton, Alan R.
    SHAPE MEMORY AND SUPERELASTICITY, 2023, 9 (01) : 97 - 115
  • [34] Tension-tension fatigue of hybrid composite rods
    Kar, N. K.
    Hu, Y.
    Barjasteh, E.
    Nutt, S. R.
    COMPOSITES PART B-ENGINEERING, 2012, 43 (05) : 2115 - 2124
  • [35] Assessment of the interlaminar behaviour of a carbon fabric reinforced thermoplastic lap shear specimen under quasi-static and tension-tension fatigue loading
    De Baere, I.
    Van Paepegem, W.
    Degrieck, J.
    POLYMER TESTING, 2013, 32 (07) : 1273 - 1282
  • [36] Tension-tension fatigue of copper thin films
    Read, DT
    INTERNATIONAL JOURNAL OF FATIGUE, 1998, 20 (03) : 203 - 209
  • [37] Tension-tension fatigue behaviour of woven hemp fibre reinforced epoxy composite: A multi-instrumented damage analysis
    de Vasconcellos, Davi S.
    Touchard, Fabienne
    Chocinski-Arnault, Laurence
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 59 : 159 - 169
  • [38] Influence of specimen size on the tension-tension fatigue behaviour of fibre-reinforced plastics at room temperature and at 77 K
    Rosenkranz, P
    Humer, K
    Weber, HW
    CRYOGENICS, 2000, 40 (03) : 155 - 158
  • [39] A comparative study of twill weave reinforced composites under tension-tension fatigue loading: Experiments and meso-modelling
    Xu, J.
    Lomov, S. V.
    Verpoest, I.
    Daggumati, S.
    Van Paepegem, W.
    Degrieck, J.
    COMPOSITE STRUCTURES, 2016, 135 : 306 - 315
  • [40] Fatigue failure mechanism analysis and life prediction of short fiber reinforced polymer composites under tension-tension loading
    Zhang, Lei
    Li, Zeyang
    Zhang, Hanyu
    Liu, Zhao
    Zhu, Ping
    INTERNATIONAL JOURNAL OF FATIGUE, 2022, 160