STRESS CORROSION CRACKING RESISTANCE OF ALUMINUM ALLOY 7000 SERIES AFTER TWO-STEP AGING

被引：2
|
作者：
Jegdic, Bore V. [1 ]
Bobic, Biljana M. [1 ]
Pavlovic, Milos K. [2 ]
Alil, Ana B. [3 ]
Putic, Slavisa S. [4 ]
机构：
[1] Univ Belgrade, Inst Chem Technol & Met, Belgrade, Serbia
[2] Welding Inst, Belgrade, Serbia
[3] Univ Belgrade, Fac Technol & Met, Innovat Ctr, Belgrade 11000, Serbia
[4] Univ Belgrade, Fac Technol & Met, Belgrade 11000, Serbia
来源：
CHEMICAL INDUSTRY & CHEMICAL ENGINEERING QUARTERLY | 2015年 / 21卷 / 02期
关键词：
aluminum alloys; stress corrosion cracking; aging; mechanical properties; MG-CU ALLOY;
D O I：
10.2298/CICEQ140324024J
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
The effect of one-step and a new (short) two-step aging process on the resistance to stress corrosion cracking of an aluminum alloy 7000 series was investigated, using slow strain rate test and fracture mechanics method The aging level in the tested alloy was evaluated by means of scanning electron microscopy and measurements of electrical resistivity. It was shown that the alloy after the new two-step aging is significantly more resistant to stress corrosion cracking. Values of tensile properties and fracture toughness are similar for both thermal states. Processes that take place at the crack tip have been considered. The effect of the testing solution temperature on the crack growth rate on the plateau was determined. Two values of the apparent activation energy were obtained. These values correspond to different processes that control crack growth rate on the plateau at higher and lower temperatures.
引用
收藏
页码：261 / 268
页数：8
相关论文
共 50 条
  • [41] STRESS-CORROSION CRACKING OF AN ALUMINUM-ALLOY UNDER COMPRESSIVE STRESS
    CHU, WY
    HSIAO, CM
    WANG, JW
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1985, 16 (09): : 1663 - 1670
  • [42] Influence of two-step aging on structure and stress corrosion sensitivity of friction stir welded 7050-T7451 aluminum alloys
    Zhang H.
    Guo Q.
    Zhao C.
    Lin S.
    Shi G.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2020, 41 (06): : 1 - 5
  • [43] Influence of two-step aging on structure and stress corrosion sensitivity of friction stir welded 7050-T7451 aluminum alloys
    张华
    郭启龙
    赵常宇
    林三宝
    石功奇
    China Welding, 2020, 29 (04) : 1 - 6
  • [44] RESEARCH OF HYDROGEN INDUCED CRACKING AND STRESS-CORROSION CRACKING IN AN ALUMINUM-ALLOY
    CHU, WY
    WANG, YB
    HSIAO, CM
    CORROSION, 1982, 38 (11) : 561 - 570
  • [45] Improving the Corrosion Resistance of Aluminum Alloy by Creating a Superhydrophobic Surface Structure through a Two-Step Process of Etching Followed by Polymer Modification
    Shi, Tian
    Liang, Jingsong
    Li, Xuewu
    Zhang, Chuanwei
    Yang, Hejie
    POLYMERS, 2022, 14 (21)
  • [46] Effects of Two-Step Aging Temperature on Exfoliation Corrosion of an Al-Zn-Mg-Cu Alloy
    Chen, Xu
    Liu, Zhiyi
    Lin, Lianghua
    Bai, Song
    ADVANCED ENGINEERING MATERIALS, PTS 1-3, 2011, 194-196 : 1338 - 1341
  • [47] THE EFFECTS OF THERMAL TREATMENTS ON THE STRESS-CORROSION CRACKING RESISTANCE OF FORGINGS OF THE ALUMINUM-ALLOY-7010
    ROBINSON, J
    FLYNN, P
    ADVANCES IN ENGINEERING MATERIALS, 1995, 99-1 : 143 - 149
  • [48] EFFECT OF EXTRUSION PROCESS ON THE STRESS CORROSION CRACKING RESISTANCE OF 7N01 ALUMINUM ALLOY
    Xie, H.
    Yang, Z.
    Ma, Q. -S.
    Meng, W.
    Hu, L.
    Yin, X. -H.
    JOURNAL OF MINING AND METALLURGY SECTION B-METALLURGY, 2023, 59 (01) : 137 - 146
  • [49] Stress corrosion cracking susceptibility of 7A52 aluminum alloy
    赵军军
    王卫欣
    蔡志海
    张平
    TransactionsofNonferrousMetalsSocietyofChina, 2006, (S3) : 1523 - 1527
  • [50] A NEW MODEL FOR STRESS-CORROSION CRACKING IN 7075 ALUMINUM ALLOY
    JACOBS, AJ
    ASM TRANSACTIONS QUARTERLY, 1966, 59 (03): : 585 - &
12345