Cooling rate and microstructure of rapidly solidified Al-20 wt.% Si alloy

被引：92

作者：

Xu, CL ^{[1
]}

Wang, HY ^{[1
]}

Qiu, F ^{[1
]}

Yang, YF ^{[1
]}

Jiang, QC ^{[1
]}

机构：

[1] Jilin Univ, Dept Mat Sci & Engn, Minist Educ, Key Lab Automobile Mat, Changchun 130025, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2006年 / 417卷 / 1-2期

基金：

中国国家自然科学基金;

关键词：

melt-spun ribbon; temperature distribution; cooling rate; Al-Si alloys;

D O I：

10.1016/j.msea.2005.10.040

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A 40 mu m thick melt-spun ribbon was manufactured by using a single roller melt-spinning technique, and the temperature distribution of the melt-spun ribbon was obtained. The solidification time and the cooling rate of the melt-spun ribbon were estimated to be 6.59 x 10(-5) s and 1.11 X 10(6) degrees C/s, respectively. The morphologies of primary silicon in the melt-spun ribbon were drastically changed to fine block-shape (maximum size of primary silicon is 5 mu m, minimum size of primary silicon is 0.5 mu m and average size of primary silicon is 2 mu m), and the smaller eutectic silicon can be obtained due to the rapid solidification. (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：275 / 280

页数：6

共 50 条

[21] Effect of increasing the cooling rate upon solidification on the microstructure and microhardness of a hypereutectic Al-Si alloy containing 29 wt. % Si
UPB Sci Bull Ser B, 1-4 (77-84):
[22] Microstructure and mechanical properties of rapidly solidified Al-20Si-xFe-3Cu-lMg (x=0 and 5 wt.%) Extradates
T. S. Kim
K. H. Kim
W. T. Kim
C. W. Won
S. S. Cho
B. S. Chun
Metals and Materials, 1998, 4 : 1163 - 1169
[23] Effect of cooling rate and Mg addition on the structural evaluation of rapidly solidified Al-20wt%Cu-12wt%Fe alloy
Karakose, Ercan
Colak, Hakan
MATERIALS CHARACTERIZATION, 2016, 121 : 68 - 75
[24] Effect of Al-P-Ti-TiC-Nd2O3 modifier on the microstructure and mechanical properties of hypereutectic Al-20 wt. %Si alloy
Xu, C. L.
Wang, H. Y.
Yang, Y. F.
Jiang, Q. C.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 452 : 341 - 346
[25] Microstructure and mechanical properties of rapidly solidified Al-20Si-xFe-3Cu-1Mg (x=0 and 5 wt.%) extrudates
Kim, T.S.
Kim, K.H.
Kim, W.T.
Won, C.W.
Cho, S.S.
Chun, B.S.
Metals and Materials International, 1998, 4 (06): : 1163 - 1169
[26] Microstructure and mechanical properties of rapidly solidified Al-20Si-xFe-3Cu-1Mg (x=0 and 5 wt.%) extrudates
Kim, TS
Kim, KH
Kim, WT
Won, CW
Cho, SS
Chun, BS
METALS AND MATERIALS-KOREA, 1998, 4 (06): : 1163 - 1169
[27] Mechanical properties and fracture mechanism of nanostructured Al-20 wt% Si alloy
Hong, SJ
Suryanarayana, C
PROCESSING AND PROPERTIES OF STRUCTURAL NANOMATERIALS, 2003, : 133 - 140
[28] Microstructure and phase structure of rapidly solidified Al-Si alloy
Key Laboratory of Material Physics, Zhengzhou University, Zhengzhou 450052, China
不详
Cailiao Rechuli Xuebao, 2008, 2 (99-102):
[29] Formation of the microstructure of rapidly solidified hypoeutectic Al-Si alloy
Olga Gusakova
Vasiliy Shepelevich
Dmitri V. Alexandrov
Ilya O. Starodumov
The European Physical Journal Special Topics, 2020, 229 : 417 - 425
[30] Formation of the microstructure of rapidly solidified hypoeutectic Al-Si alloy
Gusakova, Olga
Shepelevich, Vasiliy
Alexandrov, Dmitri V.
Starodumov, Ilya O.
EUROPEAN PHYSICAL JOURNAL-SPECIAL TOPICS, 2020, 229 (2-3): : 417 - 425

← 1 2 3 4 5 →