Carbothermal synthesis of ZrC powders using a combustion synthesis precursor

被引：36

作者：

Chu, Aimin ^{[1
,2
]}

Qin, Mingli ^{[1
]}

Rafi-ud-din ^{[3
]}

Zhang, Lin ^{[1
]}

Lu, Huifeng ^{[1
]}

Jia, Baorui ^{[1
]}

Qu, Xuanhui ^{[1
]}

机构：

[1] Univ Sci & Technol Beijing, Sch Mat Sci & Engn, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China

[2] Hunan Univ Sci & Technol, Sch Electromech Engn, Xiangtan 411201, Peoples R China

[3] PINSTECH, Div Chem, Islamabad, Pakistan

来源：

INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS | 2013年 / 36卷

关键词：

ZrC powders; Carbothermal reduction; Combustion synthesis; Precursor; ZIRCONIUM CARBIDE; REDUCTION; TITANIUM; HAFNIUM; CARBON;

D O I：

10.1016/j.ijrmhm.2012.08.016

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

ZrC powders were synthesized by carbothermal reduction of a combustion synthesized precursor derived from zirconium nitrate, urea, and glucose mixed solution. The results showed that the obtained precursor was comprised of polyporous blocky particles. The precursor powders were subsequently calcined under argon at 1200-1600 degrees C for 3 h. The transformation of ZrO2 to ZrC, by adopting this route, occurred at 1300 degrees C. The preparation of ZrC experienced an intermediate phase of ZrOxCy. ZrC powders synthesized at 1500 degrees C are characterized by the spherical shape, small particle size (120-180 nm in diameter), low oxygen content (1.4 wt.%) and non-aggregated particles. (C) 2012 Elsevier Ltd. All rights reserved.

引用

页码：204 / 210

页数：7

共 50 条

[41] Effects of Starting Carbon Sources on the Carbothermal Synthesis of SiC Powders
Cheng Junhua
Wen Dijiang
CHINESE CERAMICS COMMUNICATIONS, 2010, 105-106 : 754 - +
[42] Carbothermal Reduction Synthesis of Zirconium Diboride Powders Assisted by Microwave
Wang Hailong
Zhang Shixun
Chen Deliang
Han Qianfei
Lu Hongxia
Xu Hongliang
Wang, Chang-An
Rui, Zhang
CHINESE CERAMICS COMMUNICATIONS, 2010, 105-106 : 203 - +
[43] Synthesis of nano-sized SiC powders by carbothermal reduction
Yoshioka, Yoshiki
Tanaka, Hidehiko
Konishi, Mikio
Nishimura, Toshiyuki
Key Engineering Materials, 2009, 403 : 211 - 214
[44] Synthesis of ZrC-SiC Powders by a Preceramic Solution Route
Cai, Tao
Qiu, Wen-Feng
Liu, Dan
Han, Wei-Jian
Ye, Li
Zhao, Ai-Jun
Zhao, Tong
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 2013, 96 (10) : 3023 - 3026
[45] Direct combustion synthesis of SiC powders
Wu, CC
Chen, CC
JOURNAL OF MATERIALS SCIENCE, 1999, 34 (17) : 4357 - 4363
[46] Direct combustion synthesis of SiC powders
Chien-Chun Wu
Chien-Chong Chen
Journal of Materials Science, 1999, 34 : 4357 - 4363
[47] Combustion synthesis of V(CN) powders
Mu, Yunchao
Liang, Baoyan
MANAGEMENT, MANUFACTURING AND MATERIALS ENGINEERING, PTS 1 AND 2, 2012, 452-453 : 278 - 281
[48] Combustion synthesis of nanosized SiCxNy powders
Keil, DG
Calcote, HF
Gill, RJ
COVALENT CERAMICS III - SCIENCE AND TECHNOLOGY OF NON-OXIDES, 1996, 410 : 161 - 166
[49] COMBUSTION SYNTHESIS OF METAL CHROMITE POWDERS
MANOHARAN, SS
PATIL, KC
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1992, 75 (04) : 1012 - 1015
[50] Synthesis of Nano-Size AlN Powders by Carbothermal Reduction from Plasma-Assisted Ball Milling Precursor
Liu Zhijie
Wang Wenchun
Yang Dezheng
Wang Sen
Dai Leyang
PLASMA SCIENCE & TECHNOLOGY, 2016, 18 (07) : 759 - 763

← 1 2 3 4 5 →