Static and fatigue failure analysis of adhesively bonded thick composite single lap joints

被引：58

作者：

Tang, J. H. ^{[1
]}

Sridhar, I. ^{[1
,2
]}

Srikanth, N. ^{[2
]}

机构：

[1] Nanyang Technol Univ, Sch Mech & Aerosp Engn, Singapore 639798, Singapore

[2] Nanyang Technol Univ, Energy Res Inst, Singapore 637141, Singapore

来源：

COMPOSITES SCIENCE AND TECHNOLOGY | 2013年 / 86卷

关键词：

Adhesive joints; Fatigue; Interface; Finite element analysis; STRESS SINGULARITY APPROACH; BONDLINE THICKNESS; STRUCTURAL ADHESIVES; INTENSITY FACTORS; FRACTURE; BEHAVIOR; PREDICTION; INITIATION; CRITERION; STRENGTH;

D O I：

10.1016/j.compscitech.2013.06.018

中图分类号：

TB33 [复合材料];

学科分类号：

摘要：

Static and fatigue behavior of thick composite laminate single lap joints with thick adhesive bondline is experimentally and numerically investigated. Stress based analysis is used to understand the uniaxial tensile behavior of thick glass fiber reinforced epoxy laminates bonded with relatively thick epoxy adhesive. The effect of adhesive thickness on relatively thick adherend on the fatigue initiation life was modeled with generalized stress singularity approach. It was observed that the failure onset always occurred at adherend-adhesive interface. Subsequent crack propagation mostly resulted in interlaminar failure of adjacent first angle ply near to this interface. Both static and fatigue strength values decrease with increase of bondline thickness. Evaluation of generalized stress intensity factors of the corner geometry (square edge joint) provided a good correlation between predictions and experimental measurements. (C) 2013 Elsevier Ltd. All rights reserved.

引用

页码：18 / 25

页数：8

共 50 条

[31] Stress analysis of generally asymmetric single lap adhesively bonded joints
Lee, J
Kim, H
JOURNAL OF ADHESION, 2005, 81 (05): : 443 - 472
[32] Finite Element Analysis of Adhesively Bonded Single-lap Joints
He, Xiaocong
MATERIALS AND MANUFACTURING TECHNOLOGY, PTS 1 AND 2, 2010, 129-131 : 411 - 415
[33] EXPERIMENTAL INVESTIGATION OF THE STATIC TORQUE TRANSMISSION CAPABILITIES OF THE ADHESIVELY BONDED SINGLE LAP JOINTS
CHOI, JK
LEE, DG
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 1995, 48 (1-4) : 341 - 347
[34] Experimental and numerical investigation of adhesively bonded single lap and thick adherents joints between pultruded GFRP composite profiles
Ungureanu, Dragos
Taranu, Nicolae
Lupasteanu, Vlad
Isopescu, Donna Nicolina
Oprisan, Gabriel
Mihai, Petru
COMPOSITES PART B-ENGINEERING, 2018, 146 : 49 - 59
[35] EXPERIMENTAL RESEARCH ON FATIGUE BEHAVIOR OF ADHESIVELY BONDED STEEL SINGLE-LAP JOINTS
Jiang, Xiaoli
Kaminski, Miroslaw Lech
PROCEEDINGS OF THE ASME 31ST INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE AND ARCTIC ENGINEERING, 2012, VOL 6, 2012, : 21 - 27
[36] The effects of adherend thickness on the fatigue strength of adhesively bonded single-lap joints
Sahin, Resul
Akpinar, Salih
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2021, 107
[37] An assessment of failure criteria to predict the strength of adhesively bonded composite double lap joints
Tong, L
JOURNAL OF REINFORCED PLASTICS AND COMPOSITES, 1997, 16 (08) : 698 - 713
[38] Durability aspects of adhesively bonded thick adherend lap shear joints
Knox, EM
Cowling, MJ
INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2000, 20 (04) : 323 - 331
[39] Failure mechanism of single lap, adhesively bonded composite-titanium joints subjected to solid projectile impact
He, Boling
Pan, Yingguang
JOURNAL OF ADHESION SCIENCE AND TECHNOLOGY, 2022, 36 (04) : 370 - 391
[40] Degradation of single lap adhesively bonded composite joints due to hot water ageing
Soykok, Ibrahim Fadil (ifsoykok@gmail.com), 1600, Bellwether Publishing, Ltd. (93):

← 1 2 3 4 5 →