Synergistic effect of nanoflaky manganese phosphate on thermal degradation and flame retardant properties of intumescent flame retardant polypropylene system

Nanoflaky manganese phosphate (NMP) was synthesized from manganese nitrate and trisodium phosphate dodecahydrate, and used as a synergistic agent on the flame retardancy of polypropylene (PP)/intumescent flame retardant (IFR) system. The thermogravimetric analysis (TGA), real time Fourier-transform infrared (RTFTIR) spectroscopy measurements, cone calorimeter (CONE) and microscale combustion calorimeter (MCC) were used to evaluate the synergistic effects of NMP on PP/IFR system. When IFR + NMP was fixed at 20 wt% in flame retardant PP system, the TGA tests showed that NMP could enhance the thermal stability of PP/IFR system at initial temperature from about room temperature to 440 degrees C and effectively increase the char residue formation. The RTFTIR results revealed that NMP could clearly change the decomposition behavior of PP in PP/IFR system, which promotes decomposition at the initial temperature from about room temperature to 260 degrees C and forms more effective barrier layer to protect PP from decomposing at high temperature from about 260 degrees C to 500 degrees C. The CONE tests indicated that the addition of NMP in PP/IFR system not only reduced the peak heat release rate (HRR), but also prolonged the ignition time. The MCC results revealed that PP/IFR/NMP system generated less combustion heat over the course of heating than that of PP/IFR system. And scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) were used to explore the char residues of the PP/IFR systems with and Without NMR. (C) 2008 Elsevier Ltd. All rights reserved.