Effects of sodium tartrate anodizing on fatigue life of TA15 titanium alloy

被引：2
|
作者：
Fu Chunjuan [1 ]
Tian Wenming [1 ]
Yang Kang [1 ]
Yu Mei [1 ]
Liu Jianhua [1 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
来源：
CHINESE JOURNAL OF AERONAUTICS | 2015年 / 28卷 / 04期
基金：
中国国家自然科学基金;
关键词：
Anodic oxidation; Fatigue; Hydrogen; Sodium tartrate; Titanium alloy; CYCLIC DEFORMATION-BEHAVIOR; HYDROGEN EMBRITTLEMENT; PITTING CORROSION; SURFACE; 304-STAINLESS-STEEL; ROUGHNESS; GROWTH; DAMAGE; FILMS;
D O I：
10.1016/j.cja.2015.02.014
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
Anodizing is always used as an effective surface modification method to improve the corrosion resistance and wear resistance of titanium alloy. The sodium tartrate anodizing is a new kind of environmental anodizing method. In this work, the effects of sodium tartrate anodizing on mechanical property were studied. The oxide film was performed on the TA15 titanium alloy using sodium tartrate as the film former. The effects of this anodizing and the traditional acid anodizing on the fatigue life of TA15 alloy were compared. The results show that the sodium tartrate anodizing just caused a slight increase of hydrogen content in the alloy, and had a slight effect on the fatigue life. While, the traditional acid anodizing caused a significant increase of hydrogen content in the substrate and reduced the fatigue life of the alloy significantly. (C) 2015 Production and hosting by Elsevier Ltd.
引用
收藏
页码：1281 / 1286
页数：6
相关论文
共 50 条
  • [21] Relationship of fatigue crack propagation and microstructure for TA15 alloy
    Wu, Chongzhou
    Li, Xingwu
    Huang, Xu
    Ma, Jimin
    Cao, Chunxiao
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2007, 36 (12): : 2128 - 2131
  • [22] Low-cycle fatigue behavior and life prediction of TA15 titanium alloy by crystal plasticity-based modelling
    Li, Yanxi
    Zhan, Mei
    Jiang, Xueqi
    Lei, Yudong
    Gao, Pengfei
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2023, 23 : 954 - 966
  • [23] The effect of porosity on the fatigue crack growth behavior of selective laser melted TA15 titanium alloy
    Wang, Lei
    Feng, Shengzhou
    Wang, Yonggang
    Ge, Jiaxing
    Gao, Tianxi
    Wang, Taolei
    ENGINEERING FAILURE ANALYSIS, 2025, 170
  • [24] Study on fatigue crack propagation behavior of TA15 titanium alloy repaired by laser deposition repair
    Zhou, Song
    An, Jinlan
    Wang, Xiangming
    Xie, Li-yang
    Xu, Xingyuan
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (12) : 3692 - 3700
  • [25] Microstructure and Fatigue Properties of Laser Deposition Repaired TA15 Titanium Alloy Manufactured by Laser Deposition
    Wang W.
    Li X.
    Zhao S.
    Fan R.
    Yang G.
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2019, 43 (10): : 1047 - 1053
  • [26] Constitutive equation and hot processing map of TA15 titanium alloy
    Ji, Hongchao
    Peng, Zhanshuo
    Pei, Weichi
    Xin, Long
    Ma, Zheng
    Lu, Yonghao
    MATERIALS RESEARCH EXPRESS, 2020, 7 (04)
  • [27] Research on the microstructure and properties of weld repairs in TA15 titanium alloy
    Liu Liming
    Du Xin
    Zhu Meili
    Chen Guoqing
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 445 : 691 - 696
  • [28] Modeling of grain growth for dynamic recrystallization of TA15 titanium alloy
    Ouyang, Delai
    Lu, Shiqiang
    Cui, Xia
    Wu, Chao
    Li, Xin
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (07): : 1162 - 1165
  • [29] Ductile fracture behavior of TA15 titanium alloy at elevated temperatures
    Lei Yang
    Bao-yu Wang
    Jian-guo Lin
    Hui-jun Zhao
    Wen-yu Ma
    InternationalJournalofMineralsMetallurgyandMaterials, 2015, 22 (10) : 1082 - 1091
  • [30] Oxidation behaviors of TA15 titanium alloy and TiBw reinforced TA15 matrix composites prepared by spark plasma sintering
    Dongjun Wang
    Hao Li
    Wei Zheng
    Journal of Materials Science & Technology, 2020, 37 (02) : 46 - 54
12345