Effects of sodium tartrate anodizing on fatigue life of TA15 titanium alloy

被引：2
|
作者：
Fu Chunjuan [1 ]
Tian Wenming [1 ]
Yang Kang [1 ]
Yu Mei [1 ]
Liu Jianhua [1 ]
机构：
[1] Beijing Univ Aeronaut & Astronaut, Sch Mat Sci & Engn, Beijing 100191, Peoples R China
来源：
CHINESE JOURNAL OF AERONAUTICS | 2015年 / 28卷 / 04期
基金：
中国国家自然科学基金;
关键词：
Anodic oxidation; Fatigue; Hydrogen; Sodium tartrate; Titanium alloy; CYCLIC DEFORMATION-BEHAVIOR; HYDROGEN EMBRITTLEMENT; PITTING CORROSION; SURFACE; 304-STAINLESS-STEEL; ROUGHNESS; GROWTH; DAMAGE; FILMS;
D O I：
10.1016/j.cja.2015.02.014
中图分类号：
V [航空、航天];
学科分类号：
08 ; 0825 ;
摘要：
Anodizing is always used as an effective surface modification method to improve the corrosion resistance and wear resistance of titanium alloy. The sodium tartrate anodizing is a new kind of environmental anodizing method. In this work, the effects of sodium tartrate anodizing on mechanical property were studied. The oxide film was performed on the TA15 titanium alloy using sodium tartrate as the film former. The effects of this anodizing and the traditional acid anodizing on the fatigue life of TA15 alloy were compared. The results show that the sodium tartrate anodizing just caused a slight increase of hydrogen content in the alloy, and had a slight effect on the fatigue life. While, the traditional acid anodizing caused a significant increase of hydrogen content in the substrate and reduced the fatigue life of the alloy significantly. (C) 2015 Production and hosting by Elsevier Ltd.
引用
收藏
页码：1281 / 1286
页数：6
相关论文
共 50 条
  • [1] Effects of sodium tartrate anodizing on fatigue life of TA15 titanium alloy
    Fu Chunjuan
    Tian Wenming
    Yang Kang
    Yu Mei
    Liu Jianhua
    Chinese Journal of Aeronautics, 2015, 28 (04) : 1281 - 1286
  • [2] Effects of sodium tartrate anodizing on fatigue life of TA15 titanium alloy
    Fu Chunjuan
    Tian Wenming
    Yang Kang
    Yu Mei
    Liu Jianhua
    Chinese Journal of Aeronautics , 2015, (04) : 1281 - 1286
  • [3] Fatigue Properties of Laser Deposited Repaired TA15 Titanium Alloy
    Hui, Li (syhuili@126.com), 1943, Science Press (46):
  • [4] Stochastic Characteristics of Fatigue Crack Propagation for TA15 Titanium Alloy
    Bao Rui
    Zhang Jianyu
    Yang Hongqin
    Fei Binjun
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS VIII, 2010, 417-418 : 873 - 876
  • [5] Fatigue Properties of Laser Deposited Repaired TA15 Titanium Alloy
    Xu Liang
    Huang Shuangjun
    Wang Lei
    Zhou Song
    Hui Li
    RARE METAL MATERIALS AND ENGINEERING, 2017, 46 (07) : 1943 - 1948
  • [6] Effects of microstructure on the dynamic properties of TA15 titanium alloy
    Arab, Ali
    Chen Pengwan
    Guo Yansong
    MECHANICS OF MATERIALS, 2019, 137
  • [7] Effect of structure on fatigue properties and fracture toughness for TA15 titanium alloy
    Beijing Institute of Aeronautical Materials, Beijing 100095, China
    Cailiao Gongcheng, 2007, 7 (3-5): : 3 - 5
  • [8] A novel probability density model for random vibration fatigue life prediction of TA15 titanium alloy
    Qiu, Zhiyong
    He, Huan
    Wang, Zhanyi
    Zhang, Xiangnan
    Lv, Cheng
    ENGINEERING FRACTURE MECHANICS, 2025, 317
  • [9] Fatigue Behavior of Laser Metal Deposition TA15 Titanium Alloy Universal Beam
    Wu, Bin
    Tang, Dingcheng
    He, Xiaofan
    Wang, Tianshuai
    Zhang, Xin
    Li, Yuhai
    Xiyou Jinshu/Chinese Journal of Rare Metals, 2022, 46 (05): : 545 - 553
  • [10] Technology of corrosion processing of TA15 titanium alloy
    Lin, Cui
    Liang, Jing
    Zhao, Qing
    Du, Nan
    Wang, Li-Qiang
    Cailiao Gongcheng/Journal of Materials Engineering, 2010, (08): : 51 - 55
12345