The heat dissipation at fatigue crack tip under mix mode loading

被引：1
|
作者：
Plekhov, O. [1 ]
Vshivkov, A. [1 ]
Iziumova, A. [1 ]
Zakharov, A. [2 ]
Shlyannikov, V. [2 ]
机构：
[1] Russian Acad Sci, Ural Branch, Inst Continuous Media Mech, Ac Koroleva St 1, Perm 614013, Russia
[2] Russian Acad Sci, Kazan Sci Ctr, Lobachevskogo Str 2-31, Kazan 420111, Russia
来源：
ECF22 - LOADING AND ENVIRONMENTAL EFFECTS ON STRUCTURAL INTEGRITY | 2018年 / 13卷
基金：
俄罗斯基础研究基金会;
关键词：
energy dissipation; crack propagation; infrared thermography; mix mode loading; ENERGY; DEFORMATION;
D O I：
10.1016/j.prostr.2018.12.249
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The cruciform plane specimens of titanium alloy VT1-0 with a thick of 1 mm were tested to study temperature evolution under fatigue crack propagation. The original contact sensor of heat flow and method of infrared thermography were used to analyze the dissipated energy from crack tip during fatigue tests. A series of experiments was carried out to study the propagation of a fatigue crack under biaxial loading with different biaxial coefficient. It has been shown that heat dissipation caused by fatigue crack propagation under Paris regime can be divided into two stages both under uniaxial and biaxial loading conditions. (C) 2018 The Authors. Published by Elsevier B.V.
引用
收藏
页码：1209 / 1214
页数：6
相关论文
共 50 条
  • [31] CRACK TIP HEATING IN SHORT-FIBER COMPOSITES UNDER FATIGUE LOADING CONDITIONS
    LANG, RW
    MANSON, JA
    JOURNAL OF MATERIALS SCIENCE, 1987, 22 (10) : 3576 - 3580
  • [32] Estimation of Crack Tip Position in Adhesively Bonded Joints Subjected to Mode II Fatigue Loading
    Mehrabi, M.
    Martulli, L. M.
    Bernasconi, A.
    Carboni, M.
    SENSORS, 2024, 24 (23)
  • [33] Energy dissipation in mode II fatigue crack growth
    Amaral, Lucas
    Zarouchas, Dimitrios
    Alderliesten, Rene
    Benedictus, Rinze
    ENGINEERING FRACTURE MECHANICS, 2017, 173 : 41 - 54
  • [34] Delamination crack tip behavior at failure in composite laminates under mode I loading
    Paris, Isabelle
    Poursartip, Anoush
    1998, Technomic Publ Co Inc, Lancaster, PA, United States (11)
  • [35] Delamination crack tip behavior at failure in composite laminates under mode I loading
    Paris, I
    Poursartip, A
    JOURNAL OF THERMOPLASTIC COMPOSITE MATERIALS, 1998, 11 (01) : 57 - 69
  • [36] Transient dislocation emission from a crack tip under dynamic mode II loading
    G.-Y. Huang
    Y.-S. Wang
    D. Gross
    Zeitschrift für angewandte Mathematik und Physik ZAMP, 2002, 53 : 839 - 854
  • [37] Asymptotic crack-tip fields in perfect plasticity under mixed mode loading
    Stepanova, L., V
    Zhabbarov, R. M.
    1ST VIRTUAL EUROPEAN CONFERENCE ON FRACTURE - VECF1, 2020, 28 : 1781 - 1786
  • [38] Transient dislocation emission from a crack tip under dynamic mode II loading
    Huang, GY
    Wang, YS
    Gross, D
    ZEITSCHRIFT FUR ANGEWANDTE MATHEMATIK UND PHYSIK, 2002, 53 (05): : 839 - 854
  • [39] Transient dislocation emission from a crack tip under dynamic mode III loading
    Wang, YS
    Gross, D
    Huang, GY
    ARCHIVE OF APPLIED MECHANICS, 2001, 71 (08) : 567 - 576
  • [40] Invariant points on energy contours around a crack tip under mixed mode loading
    Boniface, V
    Simha, KRY
    INTERNATIONAL JOURNAL OF FRACTURE, 1997, 86 (04) : 301 - 325
12345