The heat dissipation at fatigue crack tip under mix mode loading

被引:1
|
作者
Plekhov, O. [1 ]
Vshivkov, A. [1 ]
Iziumova, A. [1 ]
Zakharov, A. [2 ]
Shlyannikov, V. [2 ]
机构
[1] Russian Acad Sci, Ural Branch, Inst Continuous Media Mech, Ac Koroleva St 1, Perm 614013, Russia
[2] Russian Acad Sci, Kazan Sci Ctr, Lobachevskogo Str 2-31, Kazan 420111, Russia
基金
俄罗斯基础研究基金会;
关键词
energy dissipation; crack propagation; infrared thermography; mix mode loading; ENERGY; DEFORMATION;
D O I
10.1016/j.prostr.2018.12.249
中图分类号
TH [机械、仪表工业];
学科分类号
0802 ;
摘要
The cruciform plane specimens of titanium alloy VT1-0 with a thick of 1 mm were tested to study temperature evolution under fatigue crack propagation. The original contact sensor of heat flow and method of infrared thermography were used to analyze the dissipated energy from crack tip during fatigue tests. A series of experiments was carried out to study the propagation of a fatigue crack under biaxial loading with different biaxial coefficient. It has been shown that heat dissipation caused by fatigue crack propagation under Paris regime can be divided into two stages both under uniaxial and biaxial loading conditions. (C) 2018 The Authors. Published by Elsevier B.V.
引用
收藏
页码:1209 / 1214
页数:6
相关论文
共 50 条
  • [1] The experimental and theoretical study of heat dissipation at fatigue crack tip under biaxial loading
    Vshivkova, A.
    Iziumova, A.
    Zakharov, A.
    Shlyannikov, V
    Plekhov, O.
    THEORETICAL AND APPLIED FRACTURE MECHANICS, 2019, 103
  • [2] The effect of fatigue crack rate on the heat dissipation in metals under mixed-mode loading
    Plekhov, Oleg
    Vshivkov, Aleksei
    FRATTURA ED INTEGRITA STRUTTURALE-FRACTURE AND STRUCTURAL INTEGRITY, 2019, 13 (50): : 1 - 8
  • [3] Experimental and theoretical analysis of heat flux at fatigue crack tip under mixed mode loading
    Vshivkov, A.
    Iziumova, A.
    Yarullin, R.
    Shlyannikov, V.
    Plekhov, O.
    25TH INTERNATIONAL CONFERENCE ON FRACTURE AND STRUCTURAL INTEGRITY, 2019, 18 : 608 - 615
  • [4] Plastic dissipation in fatigue crack growth under mixed-mode loading
    Daily, JS
    Klingbeil, NW
    INTERNATIONAL JOURNAL OF FATIGUE, 2004, 26 (07) : 727 - 738
  • [5] Experimental investigation of fatigue crack induced energy dissipation under mixed mode loading
    Vshivkov, A.
    Iziumova, A.
    Plekhov, O.
    1ST VIRTUAL EUROPEAN CONFERENCE ON FRACTURE - VECF1, 2020, 28 : 1839 - 1845
  • [6] Experimental study of heat dissipation at the crack tip during fatigue crack propagation
    Vshivkov, A.
    Iziumova, A.
    Plekhov, O.
    Baer, J.
    FRATTURA ED INTEGRITA STRUTTURALE, 2016, (35): : 57 - 63
  • [7] Local crack-tip strain behavior during fatigue crack initiation under mixed mode loading
    Shimamoto, A
    Umezaki, E
    Nogata, F
    DAMAGE AND FAILURE OF INTERFACES, 1997, : 475 - 480
  • [8] Plastic dissipation energy at a bimaterial crack tip under cyclic loading
    Daily, Jeremy S.
    Klingbeil, Nathan W.
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (10) : 1710 - 1723
  • [9] About the effect of plastic dissipation in heat at the crack tip on the stress intensity factor under cyclic loading
    Ranc, N.
    Palin-Luc, T.
    Paris, P. C.
    Saintier, N.
    INTERNATIONAL JOURNAL OF FATIGUE, 2014, 58 : 56 - 65
  • [10] Numerical Simulation of Crack Tip Behavior under Fatigue Loading
    Xu, Y. G.
    Tiu, W.
    Xu, Y. Z.
    ADVANCES IN FRACTURE AND DAMAGE MECHANICS XI, 2013, 525-526 : 517 - +