Synergistic effect of interface wear and loading sequence on interface debonding and relative slipping of fiber-reinforced ceramic-matrix composites

被引：1

作者：

Li Longbiao ^{[1
]}

机构：

[1] Nanjing Univ Aeronaut & Astronaut, Coll Civil Aviat, 29 Yudao St, Nanjing 210016, Jiangsu, Peoples R China

来源：

THEORETICAL AND APPLIED FRACTURE MECHANICS | 2016年 / 86卷

关键词：

Ceramic-matrix composites (CMCs); Fatigue; Interface debonding; Interface slipping; FATIGUE HYSTERESIS BEHAVIOR; ELEVATED-TEMPERATURES; CRACKING; MECHANICS; DAMAGE; LOOPS; SHEAR;

D O I：

10.1016/j.tafmec.2016.07.002

中图分类号：

TH [机械、仪表工业];

学科分类号：

0802 ;

摘要：

This study investigates the synergistic effect of interface wear and loading sequence on interface debonding and relative slipping of fiber-reinforced ceramic-matrix composites (CMCs). There are five different fatigue loading sequences considered in the present analysis. Based on the fatigue damage mechanism of fiber slipping relative to the matrix upon unloading/reloading, the interface debonded length and interface slip lengths are determined using the fracture mechanics approach. The relationships between interface debonding, interface slipping, interface wear, cycle number, peak stress and loading sequence have been determined. The fatigue hysteresis loops of C/SiC composite under three -stage cyclic fatigue loading have been predicted using the present analysis. (C) 2016 Elsevier Ltd. All rights reserved.

引用

下载

页码：171 / 186

页数：16

共 50 条

[21] Synergistic Effects of Temperature and Oxidation on Matrix Cracking in Fiber-Reinforced Ceramic-Matrix Composites
Li Longbiao
APPLIED COMPOSITE MATERIALS, 2017, 24 (03) : 691 - 715
[22] Effects of temperature, oxidation and fiber preforms on interface shear stress degradation in fiber-reinforced ceramic-matrix composites
Li Longbiao
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 674 : 588 - 603
[23] THIXOTROPIC CASTING OF FIBER-REINFORCED CERAMIC-MATRIX COMPOSITES
RUYS, AJ
SIMPSON, SA
SORRELL, CC
JOURNAL OF MATERIALS SCIENCE LETTERS, 1994, 13 (18) : 1323 - 1325
[24] Interfacial debonding and slipping of carbon fiber-reinforced ceramic-matrix composites under two-stage cyclic loading (vol 24, pg 417, 2016)
Li, L. B.
COMPOSITE INTERFACES, 2017, 24 (05) : I - I
[25] ULTRASONIC CHARACTERIZATION OF THE FIBER-MATRIX INTERPHASE INTERFACE FOR MECHANICS OF CONTINUOUS FIBER-REINFORCED METAL-MATRIX AND CERAMIC-MATRIX COMPOSITES
KARPUR, P
MATIKAS, TE
KRISHNAMURTHY, S
COMPOSITES ENGINEERING, 1995, 5 (06): : 697 - 711
[26] Interface slip distribution of unidirectional fiber-reinforced ceramic matrix composites
Gao, X. (gaoxiguang@gmail.com), 2013, Beijing University of Aeronautics and Astronautics (BUAA) (30):
[27] Effect of Fiber Poisson Contraction on Matrix Multicracking Evolution of Fiber-Reinforced Ceramic-Matrix Composites
Li Longbiao
APPLIED COMPOSITE MATERIALS, 2015, 22 (06) : 583 - 598
[28] Effect of Fiber Poisson Contraction on Matrix Multicracking Evolution of Fiber-Reinforced Ceramic-Matrix Composites
Li Longbiao
Applied Composite Materials, 2015, 22 : 583 - 598
[29] Effect of pre-fatigue loading on tensile damage and fracture of fiber-reinforced ceramic-matrix composites
Longbiao Li
Journal of the Australian Ceramic Society, 2020, 56 : 1551 - 1573
[30] Effect of Multiple loading sequence on in-phase thermomechanical fatigue hysteresis of silicon carbide fiber-reinforced ceramic-matrix composites
Li, L.
JOURNAL OF CERAMIC SCIENCE AND TECHNOLOGY, 2018, 9 (02): : 163 - 174

← 1 2 3 4 5 →