Aluminizing of the Cr15A15 alloy surface by hot-dipping in the melt

被引：1
|
作者：
Shmorgun, V. G. [1 ]
Bogdanov, A. I. [1 ]
Slautin, O. V. [1 ]
Kulevich, V. P. [1 ]
机构：
[1] Volgograd State Tech Univ, 28 Lenina Ave, Volgograd 400005, Russia
来源：
INTERNATIONAL WORKSHOP ADVANCED TECHNOLOGIES IN MATERIAL SCIENCE, MECHANICAL AND AUTOMATION ENGINEERING - MIP: ENGINEERING - 2019 | 2019年 / 537卷
关键词：
D O I：
10.1088/1757-899X/537/2/022069
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The diffusion interraction at the interlayer boundary of the Cr15A15 alloy during aluminizing by hot-dip in a molten bath of AK12M2 silumin is investigated. It is shown that subsequent heat treatment at 1000 degrees C leads to the formation on the surface of the Cr15A15 alloy a coating of variable composition based on iron aluminides FeAl(Cr, Si) / Fe3Al(Cr, Si) / Fe(Al, Cr, Si). Grain growth in the Cr15A15 alloy and a decrease in the density of carbide inclusions with their segregation along the grain boundaries ensures a decrease in its microhardness compared to as-received condition from 2.1 to 1.6 GPa.
引用
收藏
页数：5
相关论文
共 50 条
  • [41] STRUCTURAL AND MAGNETIC-PROPERTIES IN FE70CR15B15 AMORPHOUS ALLOY
    SWIERCZEK, J
    ZBROSZCZYK, J
    CIURZYNSKA, W
    SZYMURA, S
    WYSLOCKI, B
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 1995, 140 : 319 - 320
  • [42] Effects of heat treatments on near surface elemental profiles of Fe-15Cr polycrystalline alloy
    Park, E
    Spiegel, M
    CORROSION ENGINEERING SCIENCE AND TECHNOLOGY, 2005, 40 (03) : 217 - 225
  • [43] Initial atomic-scale oxidation pathways on a Ni-15Cr(100) alloy surface
    Blades, William H.
    Barone, Matthew R.
    Reinke, Petra
    NPJ MATERIALS DEGRADATION, 2021, 5 (01)
  • [44] Initial atomic-scale oxidation pathways on a Ni–15Cr(100) alloy surface
    William H. Blades
    Matthew R. Barone
    Petra Reinke
    npj Materials Degradation, 5
  • [45] Evolution of the Multiscale Hierarchical Structure of Defects in a Melt-Quenched Fe70Cr15B15(Sn) Alloy during Low-Temperature Annealing
    Pisarenko, T. A.
    Frolov, A. M.
    Krainova, G. S.
    RUSSIAN METALLURGY, 2019, 2019 (10): : 943 - 947
  • [46] Evolution of the Multiscale Hierarchical Structure of Defects in a Melt-Quenched Fe70Cr15B15(Sn) Alloy during Low-Temperature Annealing
    T. A. Pisarenko
    A. M. Frolov
    G. S. Krainova
    Russian Metallurgy (Metally), 2019, 2019 : 943 - 947
  • [47] Hot workability and microstructure evolution of highly β stabilised Ti-25V-15Cr-0.3Si alloy
    Zeng, W. D.
    Shu, Y.
    Zhang, X. M.
    Zhou, Y. G.
    Zhao, Y. Q.
    Wu, H.
    Dai, Y.
    Yang, J.
    Zhou, L.
    MATERIALS SCIENCE AND TECHNOLOGY, 2008, 24 (10) : 1222 - 1229
  • [48] Hot workability of burn resistant Ti-35V-15Cr-0.3Si-0.1C alloy
    Zhang, S.
    Zeng, W.
    Zhou, D.
    Lai, Y.
    MATERIALS SCIENCE AND TECHNOLOGY, 2016, 32 (05) : 480 - 487
  • [49] SURFACE CHARACTERIZATION OF A RAPIDLY SOLIDIFIED A15MN25CR POWDER BEFORE AND AFTER HOT EXTRUSION
    NYLUND, A
    OLEFJORD, I
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1991, 134 : 1139 - 1143
  • [50] Study of the corrosion behavior and mechanism of a hot-dipping Zn-6Al-3Mg alloy coating in 3.5 wt% neutral NaCl solution
    Wang, Shengxing
    Ma, Xiaohan
    Bai, Jintao
    Du, Tiantian
    Ma, Ruina
    Du, An
    Zhao, Xue
    Fan, Yongzhe
    Li, Guolu
    SURFACE & COATINGS TECHNOLOGY, 2023, 464
12345