HOT DEFORMATION BEHAVIOR OF NF709 AUSTENITIC HEAT-RESISTANT STEEL

被引：0
|
作者：
Wang Jingzhong [1 ]
Wang Kuaishe [1 ]
Du Zhongze [1 ]
Liu Zhengdong [2 ]
Baohansheng [2 ]
机构：
[1] Xian Univ Architecture & Technol, Sch Met & Engn, Xian 710055, Shaanxi, Peoples R China
[2] Cent Iron & Steel Res Inst, Beijing 100081, Peoples R China
来源：
ENERGY MATERIALS CONFERENCE PROCEEDINGS 2014 | 2014年
关键词：
NF709; steel; hot compress deformation; flow stress; Z parameter; microstructure;
D O I：
暂无
中图分类号：
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号：
0807 ; 0820 ;
摘要：
The hot deformation behavior of NF709 austenitic heat-resistant steel was investigated over the temperature range of 930-1230 degrees C and strain rates range of 0.005-5 s(-1) using hot compression tests by Gleeble 3800 thermal mechanical simulator. The flow curves of tested steel were obtained corresponding to different deformation condition. The stress flow curves of tested steel were obtained and the relationship between microstructure and deformation condition were analyzed. The hot deformation activation energy of the tested steel was obtained 328kJ/mol and the hot deformation equation was established. Flow curves show that the flow instability easily occur at the strain rate of 0.005s(-1) and the temperature range from 930 degrees C to 1230 degrees C with large deformation or at relatively high temperature and 5 s(-1) with small deformation.
引用
收藏
页码：357 / 363
页数：7
相关论文
共 50 条
  • [31] Strengthening Mechanism of S30432 Austenitic Heat-resistant Steel
    Zhu, Lihui
    Zhang, Yujie
    Xu, Songqian
    Wang, Qijiang
    Lu, Zhengran
    Qi, Anfang
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2010, 29 (04) : 215 - 223
  • [32] Hot Deformation Behavior and Texture of 9Cr-2W Heat-Resistant Alloy
    Sun Shuli
    Zhang Mingang
    He Wenwu
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (11) : 1993 - 1996
  • [33] Hot deformation behavior and texture of 9Cr-2W heat-resistant alloy
    Sun, Shuli
    Zhang, Mingang
    He, Wenwu
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (11): : 1993 - 1996
  • [34] Precipitation behavior of M23C6 in high nitrogen austenitic heat-resistant steel
    Ren, Wenhao
    Wang, Limin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2022, 905
  • [35] Hot dip aluminizing of heat-resistant steel and its properties
    Hao, Jiantang
    Lu, Jie
    Kang T'ieh/Iron and Steel (Peking), 1996, 31 (12): : 45 - 48
  • [36] Hot deformation behavior of as-cast austenitic stainless steel
    Mao, Pingli
    Yang, Ke
    Su, Guoyue
    2001, Chinese Academy of Sciences (37):
  • [37] Hot deformation behavior of as-cast austenitic stainless steel
    Mao, PL
    Yang, K
    Su, GY
    ACTA METALLURGICA SINICA, 2001, 37 (01) : 39 - 41
  • [38] In situ investigation of structure and stability of niobium carbonitrides in an austenitic heat-resistant steel
    Zhang, X. F.
    Terasaki, H.
    Komizo, Y.
    SCRIPTA MATERIALIA, 2012, 67 (02) : 201 - 204
  • [39] Investigation on the strengthening mechanism of S30432 austenitic heat-resistant steel
    ZHU Lihui~(1))
    BaosteelTechnicalResearch, 2010, 4(S1) (S1) : 71 - 71
  • [40] Investigations on Strain Hardening During Cutting of Heat-Resistant Austenitic Stainless Steel
    Arif, Rabiae
    Fromentin, Guillaume
    Rossi, Frederic
    Marcon, Bertrand
    JOURNAL OF MANUFACTURING SCIENCE AND ENGINEERING-TRANSACTIONS OF THE ASME, 2020, 142 (05):
12345