Corrosion behavior of low-alloy steel in the presence of Desulfovibrio caledoniensis

被引：6
|
作者：
Cetin, D. [1 ]
Aksu, M. L. [1 ]
机构：
[1] Gazi Univ, Gazi Fac Educ, TR-06500 Ankara, Turkey
来源：
MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION | 2013年 / 64卷 / 03期
关键词：
EIS; low-alloy steel; microbial corrosion; polarization; SULFATE-REDUCING BACTERIA; STAINLESS-STEEL; DESULFOTOMACULUM SP; PASSIVE FILM; BIOFILM; SRB; BIOCORROSION; MEDIA;
D O I：
10.1002/maco.201106142
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
Sulfate-reducing bacteria (SRB) are shown to be common inhabitants of oil reservoirs. Desulfovibrio caledoniensis isolated from a production well was used in this study. After an incubation period of 1 month with the SRB culture, two layers of corrosion products with different compositions were detected on the test coupons. The Tafel plots showed that the corrosion potential exhibited a cathodic shift and the corrosion rates increased with the incubation time. The analysis of the Nyquist diagrams revealed that the diffusion process begins to dominate with time in bacteria containing medium. These results are in good accordance with the Tafel data.
引用
收藏
页码：236 / 241
页数：6
相关论文
共 50 条
  • [41] INFLUENCE OF WEATHERING ON THE CORROSION BEHAVIOR OF UNALLOYED AND LOW-ALLOY STEELS
    SCHWITTER, H
    BOHNI, H
    WERKSTOFFE UND KORROSION-MATERIALS AND CORROSION, 1980, 31 (09): : 703 - 711
  • [42] Alloying Effect of Chromium on the Corrosion Behavior of Low-Alloy Steels
    Park, S. A.
    Le, D. P.
    Kim, J. G.
    MATERIALS TRANSACTIONS, 2013, 54 (09) : 1770 - 1778
  • [43] AN INVESTIGATION OF CORROSION BEHAVIOR OF LOW-ALLOY TITANIUM-ALLOYS
    TOMASHOV, ND
    KASATKINA, IV
    SHCHERBAKOV, AI
    KOIGUSHSKII, NN
    ANOKHIN, VM
    PROTECTION OF METALS, 1989, 25 (05): : 624 - 628
  • [44] STRESS CORROSION CRACKING BEHAVIOR AROUND INTERFACE BETWEEN NICKEL BASE ALLOY (ALLOY182) AND LOW-ALLOY STEEL
    Itabashi, Yu
    Sakakibara, Yohei
    Takanashi, Masahiro
    Nakayama, Guen
    Hirano, Takashi
    PROCEEDINGS OF THE 20TH INTERNATIONAL CONFERENCE ON NUCLEAR ENGINEERING AND THE ASME 2012 POWER CONFERENCE - 2012, VOL 1, 2012, : 573 - 582
  • [45] INVESTIGATION OF STRESS-CORROSION CRACKING OF LOW-ALLOY STEEL IN WATER
    CHU, WY
    HSIAO, CM
    LI, SQ
    ENGINEERING FRACTURE MECHANICS, 1982, 16 (01) : 115 - &
  • [46] Influence factors and corrosion resistance criterion of low-alloy structural steel
    Zhao Q.-Y.
    Fan Y.
    Fan E.-D.
    Zhao B.-J.
    Huang Y.-H.
    Cheng X.-Q.
    Li X.-G.
    Gongcheng Kexue Xuebao/Chinese Journal of Engineering, 2021, 43 (02): : 255 - 262
  • [47] Microstructural Analysis of the Corrosion Products of Low-Alloy Reinforcing Steel in Concrete
    Ming J.
    Shi J.
    Sun W.
    Jianzhu Cailiao Xuebao/Journal of Building Materials, 2020, 23 (02): : 347 - 353
  • [48] Corrosion protection of steel structures by low-alloy corrosion resistant steels and surface coatings
    Matsushima, Iwao
    Zairyo to Kankyo/ Corrosion Engineering, 2004, 53 (04): : 167 - 171
  • [49] STRESS-CORROSION CRACKING OF A LOW-ALLOY STEEL IN ACETATE SOLUTIONS
    PARKER, JG
    PEARCE, WG
    CORROSION, 1974, 30 (01) : 18 - 23
  • [50] MECHANISM OF STRESS-CORROSION CRACKING OF LOW-ALLOY STEEL IN WATER
    CHU, WY
    LIU, TH
    HSIAO, CM
    LI, SQ
    CORROSION, 1981, 37 (06) : 320 - 327
12345