XRD Characterization of Microstructural Evolution During Mechanical Alloying of W-20 wt%Mo

被引：18
|
作者：
Srivastav, Ajeet K. [1 ]
Panindre, Anup M. [2 ]
Murty, B. S. [1 ]
机构：
[1] Indian Inst Technol, Dept Met & Mat Engn, Madras 600036, Tamil Nadu, India
[2] Natl Inst Technol Jamshedpur, Dept Met & Mat Engn, Jharkhand 831014, India
来源：
TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS | 2013年 / 66卷 / 04期
关键词：
Tungsten; Molybdenum; Mechanical alloying; X-ray diffraction line profile analysis; X-RAY-DIFFRACTION; TUNGSTEN; METALS; BEHAVIOR;
D O I：
10.1007/s12666-013-0269-3
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
The present paper reports a study on the microstructural evolution during mechanical alloying of W-20wt%Mo using XRD line profile analysis. The W-20wt%Mo powder blends were ball milled using Fritsch Pulverisette P-5 high energy ball mill for varying milling time (0, 5, 10, 15, 20 h) at 300 rpm with 10:1 and 2:1 ball to powder weight ratio. The crystallite size and lattice strain were calculated using Langford method ('average' Williamson-Hall Plot). The precision lattice parameter calculation was done using Nelson-Riley method. The effect of milling on alloying behaviour has been investigated using change in relative integrated intensity ratios (I (Mo) /I (W/W(Mo))) of (211) XRD peak. There was complete alloying in case of 10:1 ball to powder weight ratio, whereas half of the Mo (similar to 10 % Mo) was alloyed with 2:1 ball to powder weight ratio. The paper also discusses the applicability of the criteria based on lattice parameter change (peak shift) for alloying behaviour during mechanical milling.
引用
收藏
页码：409 / 414
页数：6
相关论文
共 50 条
  • [21] Initial stage of mechanical alloying in Fe(80)X(20) (X = Mo, W) systems
    Povstugar, IV
    Yelsukov, EP
    Butyagin, PY
    COLLOID JOURNAL, 2003, 65 (03) : 358 - 365
  • [22] Initial Stage of Mechanical Alloying in Fe(80)X(20) (X = Mo, W) Systems
    I. V. Povstugar
    E. P. Yelsukov
    P. Yu. Butyagin
    Colloid Journal, 2003, 65 : 358 - 365
  • [23] Microstructural characterizations of Ni activated sintered W-2 wt% TiC composites produced via mechanical alloying
    Genc, A.
    Coskun, S.
    Ovecoglu, M. L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2010, 497 (1-2) : 80 - 89
  • [24] Formation of intermetallic phases during mechanical alloying and annealing of Cr + 20 wt % al mixtures
    J. S. Kim
    Y. S. Kwon
    G. V. Golubkova
    O. I. Lomovsky
    D. V. Dudina
    L. S. Davlitova
    V. V. Malakhov
    S. F. Tikhov
    V. V. Usol’tsev
    V. A. Sadykov
    Inorganic Materials, 2008, 44 : 587 - 591
  • [25] Mill setting and microstructural evolution during mechanical alloying of Mg2Si
    Riffel, M
    Schilz, J
    JOURNAL OF MATERIALS SCIENCE, 1998, 33 (13) : 3427 - 3431
  • [26] Mill setting and microstructural evolution during mechanical alloying of Mg2Si
    M. Riffel
    J. Schilz
    Journal of Materials Science, 1998, 33 : 3427 - 3431
  • [27] Mill setting and microstructural evolution during mechanical alloying of Mg2Si
    Inst fuer Werkstoff-Forschung, Koeln, Germany
    J Mater Sci, 13 (3427-3431):
  • [28] Microstructural evolution and nanocrystalline formation kinetics in FeCo based alloys during mechanical alloying
    Li, HF
    Ramanujan, RV
    Science and Technology of Nanomaterials - ICMAT 2003, 2005, 23 : 187 - 190
  • [29] Formation of gradient microstructure and mechanical properties of hot-pressed W-20 wt% Cu composites after sliding friction severe deformation
    Dong, L. L.
    Ahangarkani, M.
    Zhang, W.
    Zhang, B.
    Chen, W. G.
    Fu, Y. Q.
    Zhang, Y. S.
    MATERIALS CHARACTERIZATION, 2018, 144 : 325 - 335
  • [30] Effects of rolling reduction on microstructural evolution and mechanical properties of W-0.5wt%ZrC alloys
    Zhao, B. L.
    Xia, Y. P.
    Zhang, L. F.
    Ke, J. G.
    Cheng, X.
    Xie, Z. M.
    Liu, R.
    Miao, S.
    Hao, T.
    Wu, X. B.
    Fang, Q. F.
    Liu, C. S.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 830
12345