Dark-red-emitting CdTe0.5Se0.5/Cd0.5Zn0.5S quantum dots: Effect of chemicals on properties

CdTe0.5Se0.5/Cd0.5Zn0.5S core/shell quantum dots (QDs) with a tunable photoluminescence (PL) range from yellow to dark red (up to a PL peak wavelength of 683 nm) were fabricated using various reaction systems. The core/shell QDs created in the reaction solution of trioctylamine (TOA) and oleic acid (OA) at 300 degrees C exhibited narrow PL spectra and a related low PL efficiency (38%). In contrast, the core/shell QDs prepared in the solution of 1-octadecene (ODE) and hexadecylamine (HDA) at 200 degrees C revealed a high PL efficiency (70%) and broad PL spectra. This phenomenon is ascribed that the precursor of Cd, reaction temperature, solvents, and ligands affected the formation process of the shell. The slow growth rate of the shell in the solution of ODE and HDA made QDs with a high PL efficiency. Metal acetate salts without reaction with HDA led to the core/shell QDs with a broad size distribution. (C) 2013 Elsevier B.V. All rights reserved.