Preparation of SiO2 coated Ce2S3 red pigment with improved thermal stability

被引：34
|
作者：
Chen Guanhong [1 ]
Zhu Zhenfeng [1 ]
Liu Hui [1 ]
Wu Yingfeng [1 ]
Zhu Chunkui [1 ]
机构：
[1] Shaanxi Univ Sci & Technol, Sch Mat Sci & Engn, Xian 710021, Peoples R China
来源：
JOURNAL OF RARE EARTHS | 2013年 / 31卷 / 09期
关键词：
Ce2S3; red pigment; SiO2; coating; cerium silicon molar ratio; thermal stability; rare earths; RARE-EARTH SULFIDES; STABILIZATION; GAMMA-CE2S3; GROWTH; CE; ND;
D O I：
10.1016/S1002-0721(12)60375-5
中图分类号：
O69 [应用化学];
学科分类号：
081704 ;
摘要：
SiO2 coated Ce2S3 red pigment was prepared in ethanol/H2O system via sol-gel method and TEOS were used as silica sources. X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDX), UV-visible spectrophotometer and automatic colorimeter were used to investigate the properties of the samples. The results showed that the compact SiO2 film formed on the surface of Ce2S3 pigment at a cerium silicon molar ratio of 2. The thermal stability temperature of Ce2S3 pigment was improved to 450 degrees C after SiO2 coating. In addition, the color of Ce2S3 pigment was not affected significantly through coating colorless and transparent SiO2 and it could be used as safe red pigment in higher temperature fields.
引用
收藏
页码：891 / 896
页数：6
相关论文
共 50 条
  • [21] Design and preparation of a type of γ-Ce2S3@c-SiO2-coated red pigment with a plum pudding mosaic structure: The effect of pre-sintering temperature on pigment properties
    Wu, Fuling
    Li, Xin
    Li, Yueming
    Wang, Zhumei
    Hong, Yan
    Shen, Zongyang
    Song, Fusheng
    MICROPOROUS AND MESOPOROUS MATERIALS, 2021, 311
  • [22] Stabilization of the γ-Ce2S3 phase
    Trombe, JC
    Verelst, M
    JOURNAL OF ALLOYS AND COMPOUNDS, 2001, 323 : 66 - 69
  • [23] Preparation, characterization, and photocatalytic performance of Ce2S3 for nitrobenzene reduction
    Chen, Shifu
    Zhang, Huaye
    Fu, Xianliang
    Hu, Yingfei
    APPLIED SURFACE SCIENCE, 2013, 275 : 335 - 341
  • [24] Effect of NH4F treatment on the chromaticity of the Ba2+-doped γ-Ce2S3 red pigment
    Li, Xin
    Li, Yueming
    Li, Zhike
    Wang, Zhumei
    Hong, Yan
    Song, Fusheng
    JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH, 2020, 17 (02) : 541 - 552
  • [25] Effect of NH4F treatment on the chromaticity of the Ba2+-doped γ-Ce2S3 red pigment
    Xin Li
    Yueming Li
    Zhike Li
    Zhumei Wang
    Yan Hong
    Fusheng Song
    Journal of Coatings Technology and Research, 2020, 17 : 541 - 552
  • [26] Effect of Sr2+ and Dy3+ co-doping on coloration and temperature stabilization of a γ-Ce2S3 red pigment
    Yueming Li
    Qi Liu
    Fusheng Song
    Zhumei Wang
    Zongyang Shen
    Yan Hong
    JournalofRareEarths, 2020, 38 (02) : 213 - 218
  • [27] Preparation of a microsphere SiO2/TiO2 composite pigment: The mechanism of improving pigment properties by SiO2
    Sun, Sijia
    Ding, Hao
    Wang, Jie
    Li, Wei
    Hao, Qiang
    CERAMICS INTERNATIONAL, 2020, 46 (14) : 22944 - 22953
  • [28] Research development of γ-Ce2S3
    Zhu, Z.-F., 1825, Journal of Functional Materials, P.O. Box 1512, Chongqing, 630700, China (44):
  • [29] Effect of Sr2+ and Dy3+ co-doping on coloration and temperature stabilization of a γ-Ce2S3 red pigment
    Li, Yueming
    Liu, Qi
    Song, Fusheng
    Wang, Zhumei
    Shen, Zongyang
    Hong, Yan
    JOURNAL OF RARE EARTHS, 2020, 38 (02) : 213 - 218
  • [30] Improved thermal stability of Y3Al5O12:Ce3+ phosphor by SiO2 coating
    Peng, Weikang
    Qi, Tonggang
    Zhang, Zhanhui
    Kong, Shijin
    Dai, Wubin
    Huang, Zhiliang
    SOLID STATE SCIENCES, 2019, 89 : 156 - 160
12345