Face gear surface durability investigations

Experimental fatigue tests were performed to determine the surface durability life of a face gear in mesh with a tapered spur involute pinion. Twenty-four sets of gears were tested at three load levels: 7200, 8185, and 9075 lb-inch face gear torque, and 2190-3280 rpm face gear speed. The gears were carburized and ground, shot-peened and vibro-honed, and made from vacuum induction melting-vacuum arc remelting Pyrowear 53 steel per AMS 6308. The tests produced 17 gear tooth-spalling failures and 7 suspensions. For all the failed sets, spalling occurred on at least one tooth of all the pinions. In some cases, the spalling initiated a crack in the pinion teeth that progressed to tooth fracture. Also, spalling occurred on some face gear teeth. The American Gear Manufacturing Association endurance allowable stress for a tapered spur involute pinion in mesh with a face gear was determined to be 275 ksi for the material tested.