A study of bainitic nodular cast iron for grinding balls

被引：5
|
作者：
Liu, WY [1 ]
Qu, JX [1 ]
Lin, FY [1 ]
机构：
[1] CHINA UNIV MINING & TECHNOL,BEIJING GRAD SCH,BEIJING 100083,PEOPLES R CHINA
来源：
WEAR | 1997年 / 205卷 / 1-2期
关键词：
bainite; nodular cast iron; grinding ball; nitrate solution quenching;
D O I：
10.1016/S0043-1648(96)07317-6
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
A type of C-Si-Mn nodular cast iron, used as grinding ball material, was studied. With 2.5-3.3 wt% C, 3.0-3.5 wt% Si and 2.0-2.5 wt% Mn, this type of nodular cast iron can be melted by cupola. Simple process, low cost, and high wear resistance make it more competitive as a ball material than other nodular cast irons. Heat treatment of this material was investigated at various quenching and tempering temperatures. Quenching was carried in nitrate solution. With proper quenching and tempering, the hardness of this material is higher than 50 HRC and the Mesnager impact energy is higher than 100 kN m(-1). Ball mill tests in the cement industry show the weight loss of this type of nodular cast iron is less than 100 mg for every tonne of cement ground. (C) 1997 Elsevier Science S.A.
引用
收藏
页码：97 / 100
页数：4
相关论文
共 50 条
  • [21] Energy partition for grinding of nodular cast iron with vitrified cbn wheels
    Varghese, V
    Guo, C
    Malkin, S
    Xiao, G
    MACHINING SCIENCE AND TECHNOLOGY, 2000, 4 (02) : 197 - 208
  • [22] Effect of silicon on bainitic reaction of nodular cast iron asutempered at 400pC
    Restrepo, Juan Manuel Velez
    Tschipstchin, Andre Paulo
    Metalurgia & Materiais A B M, 1993, 49 (421):
  • [23] Utilization of steel-iron scrap for manufacturing cast-forging alloy steel grinding balls and alloy cast iron grinding bars
    Luo, Yougen
    Zhang, Zhou
    Zhuzao Jishu/Foundry Technology, 1995, (06): : 29 - 31
  • [24] INFLUENCE OF AUSTEMPERING TEMPERATURE ON FRACTURE-TOUGHNESS IN BAINITIC NODULAR CAST-IRON
    DOONG, JL
    JU, FC
    CHEN, HS
    CHEN, LW
    JOURNAL OF MATERIALS SCIENCE LETTERS, 1986, 5 (05) : 555 - 558
  • [25] Microstructures and Properties of Bainitic Nodular Cast Iron Treated by Controlled cooling and austempering treatment
    Liu, Kegao
    Xu, Aimin
    Xiang, Dong
    Xu, Bin
    NEW MATERIALS AND ADVANCED MATERIALS, PTS 1 AND 2, 2011, 152-153 : 259 - 262
  • [26] Comparative analysis of two CBN grinding wheels performance in nodular cast iron plunge grinding
    de Martini Fernandes, Lucas (lucas-asewas@hotmail.com), 1600, Springer London (98): : 1 - 4
  • [27] Comparative analysis of two CBN grinding wheels performance in nodular cast iron plunge grinding
    Lucas de Martini Fernandes
    José Claudio Lopes
    Roberta Silveira Volpato
    Anselmo Eduardo Diniz
    Rodolfo Fischer Moreira de Oliveira
    Paulo Roberto de Aguiar
    Hamilton José de Mello
    Eduardo Carlos Bianchi
    The International Journal of Advanced Manufacturing Technology, 2018, 98 : 237 - 249
  • [28] Comparative analysis of two CBN grinding wheels performance in nodular cast iron plunge grinding
    Fernandes, Lucas de Martini
    Lopes, Jose Claudio
    Volpato, Roberta Silveira
    Diniz, Anselmo Eduardo
    Moreira de Oliveira, Rodolfo Fischer
    de Aguiar, Paulo Roberto
    de Mello, Hamilton Jose
    Bianchi, Eduardo Carlos
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 98 (1-4): : 237 - 249
  • [29] Technology for Making Partially Fusible Permanent Molds to Cast Iron Grinding Balls
    K. N. Vdovin
    I. V. Ponurko
    M. V. Shubina
    Metallurgist, 2001, 45 : 167 - 170
  • [30] Technology for making partially fusible permanent molds to cast iron grinding balls
    Vdovin, KN
    Ponurko, IV
    Shubina, MV
    METALLURGIST, 2001, 45 (3-4) : 167 - 170
12345