Performance of Dy2Zr2O7 Thermal Barrier Coating in Thermal-Shock Test

被引：1

作者：

Cao Xuan ^{[1
]}

Ma Zhuang ^{[1
]}

Liu Yanbo ^{[1
]}

Du Zhong ^{[1
]}

Zheng Kangnan ^{[1
]}

机构：

[1] Beijing Inst Technol, Natl Key Lab Sci & Technol Mat Shock & Impact, Beijing 100081, Peoples R China

来源：

RARE METAL MATERIALS AND ENGINEERING | 2013年 / 42卷 / 06期

关键词：

Dy2Zr2O7; thermal-shock resistance; APS; thermal barrier coating; EVOLUTION; FAILURE;

D O I：

暂无

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

A new thermal barrier coating system based on Dy2Zr2O7, which had a lower thermal conductivity and closer thermal expansion coefficient to nickel-based superalloys, was prepared by the air plasma spraying (APS). The microstructure, phase composition and thermal-shock resistance of the as-sprayed coatings were studied. Besides, the failure process of the coating during thermal cycles was also discussed. After 6 similar to 8 thermal-shock cycles, coatings spalled from the specimens. Micro cracks in the top coat grew and crushed the ceramic top coat in the vicinity of bond coat interface into pieces, and then led to the spallation of the top coat.

引用

页码：1134 / 1138

页数：5

共 50 条

[21] Thermal properties of La2Zr2O7 double-layer thermal barrier coatings
Guo, Xingye
Lu, Zhe
Park, Hye-Yeong
Li, Li
Knapp, James
Jung, Yeon-Gil
Zhang, Jing
ADVANCES IN APPLIED CERAMICS, 2019, 118 (03) : 91 - 97
[22] Performance Evaluation and Thermal Shock Behavior of PS-PVD (Gd0.9Yb0.1)2Zr2O7/YSZ Thermal Barrier Coatings
Zhao, Hongxu
Zhang, Xiaofeng
Deng, Chunming
Deng, Ziqian
Chen, Xiaolong
COATINGS, 2022, 12 (03)
[23] The Influence of Reactive PS-PVD Process Parameters on the Microstructure and Thermal Properties of Yb2Zr2O7 Thermal Barrier Coating
Pedrak, Pawel
Goral, Marek
Dychton, Kamil
Drajewicz, Marcin
Wierzbinska, Malgorzata
Kubaszek, Tadeusz
MATERIALS, 2022, 15 (04)
[24] Microstructure Evolution and Impedance Spectroscopy Characterization of Thermal Barrier Coating Exposed to Gas Thermal-shock Environment
Chen, Wen-Long
Liu, Min
Zhang, Ji-Fu
Song, Jin-Bing
Cailiao Gongcheng/Journal of Materials Engineering, 2017, 45 (10): : 79 - 87
[25] The Gd2Zr2O7-Based Materials for Thermal Barrier Coatings
E. V. Dudnik
S. N. Lakiza
N. I. Hrechanyuk
A. K. Ruban
V. P. Red’ko
M. S. Hlabay
A. B. Myloserdov
Powder Metallurgy and Metal Ceramics, 2018, 57 : 301 - 315
[26] The Gd2Zr2O7-Based Materials for Thermal Barrier Coatings
Dudnik, E. V.
Lakiza, S. N.
Hrechanyuk, N. I.
Ruban, A. K.
Red'ko, V. P.
Hlabay, M. S.
Myloserdov, A. B.
POWDER METALLURGY AND METAL CERAMICS, 2018, 57 (5-6) : 301 - 315
[27] Performance of single YSZ, Gd2Zr2O7 and double-layered YSZ/Gd2Zr2O7 thermal barrier coatings in isothermal oxidation test conditions
Doleker, Kadir Mert
Karaoglanli, Abdullah Cahit
Ozgurluk, Yasin
Kobayashi, Akira
VACUUM, 2020, 177
[28] Investigation of Thermal Shock Behavior of Nanostructured (Gd0.9Yb0.1)2Zr2O7/ YSZ Thermal Barrier Coatings
Fan W.
Bai Y.
Wang Y.
Zhongguo Xitu Xuebao/Journal of the Chinese Rare Earth Society, 2023, 41 (04): : 757 - 764
[29] Effect of Substrate Condictions on Thermal Shock Property of Plasma-spraying Sm2Zr2O7/YSZ Thermal Barrier Coatings
Zhang, Hongsong
Wei, Yuan
ADVANCED TEXTILE MATERIALS, PTS 1-3, 2011, 332-334 : 1799 - +
[30] Forming Mechanism of Dy2Ce2O7 Ceramic for Thermal Barrier Coatings
Zhang Hongsong
Hu Renxi
Xu Qiang
CHINESE CERAMICS COMMUNICATIONS, 2010, 105-106 : 383 - +

← 1 2 3 4 5 →