Mechanical properties and thermal stability of pure W and W-0.5 wt%ZrC alloy manufactured with the same technology

被引：91

作者：

Deng, H. W. ^{[1
,2
]}

Xie, Z. M. ^{[1
]}

Wang, Y. K. ^{[1
,2
]}

Liu, R. ^{[1
]}

Zhang, T. ^{[1
]}

Hao, T. ^{[1
]}

Wang, X. P. ^{[1
]}

Fang, Q. F. ^{[1
]}

Liu, C. S. ^{[1
]}

机构：

[1] Chinese Acad Sci, Inst Solid State Phys, Key Lab Mat Phys, Hefei 230031, Anhui, Peoples R China

[2] Univ Sci & Technol China, Hefei 230026, Anhui, Peoples R China

来源：

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2018年 / 715卷

基金：

中国国家自然科学基金;

关键词：

Tungsten; ZrC; Thermal stability; Mechanical property; HELIUM-COOLED DIVERTOR; GRAIN-GROWTH; DEGREES-C; TUNGSTEN; PLASMA; MICROSTRUCTURES; CONDUCTIVITY; BEHAVIOR; W-Y2O3;

D O I：

10.1016/j.msea.2017.12.112

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

The mechanical properties, microstructure and thermal stability of hot rolled pure W and W-0.5 wt%ZrC alloy manufactured using the same technology are systematically studied. The results of Vickers hardness and tensile tests show that the W-0.5 wt%ZrC alloy has a higher hardness, ultimate tensile strength, ductility and thermal stability compared to pure W. The recrystallization temperature of W-0.5 wt%ZrC alloy is about 1300 degrees C which is 100 degrees C higher than that of hot rolled pure W (1200 degrees C). The ductile to brittle transition temperature (DBTT) of W-0.5 wt%ZrC alloy is 50 degrees C lower than that of the rolled pure tungsten. The above results indicate that at the fully same fabrication technology, the trace ZrC does improve the mechanical properties and thermal stability of W. The possible micro-mechanisms were investigated and proposed.

引用

页码：117 / 125

页数：9

共 50 条

[1] Mechanical properties and thermal stability of rolled W-0.5 wt% TiC alloys
Miao, S.
Xie, Z. M.
Zhang, T.
Wang, X. P.
Fang, Q. F.
Liu, C. S.
Luo, G. N.
Liu, X.
Lian, Y. Y.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 671 : 87 - 95
[2] Oxidation behavior of pure W and W-0.5 wt% ZrC at 700 °C and 900 °C
Wang, Yongkui
Huang, Xiaochen
Lv, Changpeng
Wu, Zhong
Ge, Jinlong
Ma, Jianguo
Zhang, Xueqi
NUCLEAR MATERIALS AND ENERGY, 2025, 43
[3] Hydrogen embrittlement of bulk W-0.5 wt% ZrC alloy induced by annealing in hydrogen atmosphere
Wang, H.
Cheng, X.
Zhang, Y. G.
Wang, M. M.
Zhao, B. L.
Xie, Z. M.
Zhang, T.
Liu, R.
Wu, X. B.
Wang, X. P.
Fang, Q. F.
Chen, C. A.
Liu, C. S.
JOURNAL OF NUCLEAR MATERIALS, 2021, 556
[4] The mechanical properties and thermal stability of a nanostructured carbide. dispersion strengthened W-0.5 wt.% Ta-0.01 wt.% C alloy
Miao, S.
Xie, Z. M.
Zeng, L. F.
Zhang, T.
Fang, Q. F.
Wang, X. P.
Liu, C. S.
Luo, G. N.
Liu, X.
FUSION ENGINEERING AND DESIGN, 2017, 125 : 490 - 495
[5] Effect of hot rolling and annealing on the mechanical properties and thermal conductivity of W-0.5 wt.% TaC alloys
Miao, S.
Xie, Z. M.
Yang, X. D.
Liu, R.
Gao, R.
Zhang, T.
Wang, X. P.
Fang, Q. F.
Liu, C. S.
Luo, G. N.
Liu, X.
Lian, Y. Y.
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2016, 56 : 8 - 17
[6] Thermal shock fatigue behaviors of various W-0.5 wt%ZrC materials under repetitive transient heat loads
Wang, M. M.
Xie, Z. M.
Deng, H. W.
Liu, R.
Yang, J. F.
Zhang, T.
Wang, X. P.
Fang, Q. F.
Liu, C. S.
Liu, X.
Xiong, Y.
JOURNAL OF NUCLEAR MATERIALS, 2020, 534
[7] Mechanical properties, thermal stability and microstructure of fine-grained W-0.5 wt.% TaC alloys fabricated by an optimized multi-step process
Miao, S.
Xie, Z. M.
Zeng, L. F.
Zhang, T.
Wang, X. P.
Fang, Q. F.
Liu, C. S.
NUCLEAR MATERIALS AND ENERGY, 2017, 13 : 12 - 20
[8] Effects of rolling reduction on microstructural evolution and mechanical properties of W-0.5wt%ZrC alloys
Zhao, B. L.
Xia, Y. P.
Zhang, L. F.
Ke, J. G.
Cheng, X.
Xie, Z. M.
Liu, R.
Miao, S.
Hao, T.
Wu, X. B.
Fang, Q. F.
Liu, C. S.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2022, 830
[9] Microstructures, Mechanical Properties and Thermal Conductivities of W-0.5 wt.% TiC Alloys Prepared via Ball Milling and Wet Chemical Method
Lang, Shaoting
Yan, Qingzhi
Sun, Ningbo
Zhang, Xiaoxin
Ge, Changchun
JOM, 2017, 69 (10) : 1992 - 1996
[10] Microstructures, Mechanical Properties and Thermal Conductivities of W-0.5 wt.%TiC Alloys Prepared via Ball Milling and Wet Chemical Method
Shaoting Lang
Qingzhi Yan
Ningbo Sun
Xiaoxin Zhang
Changchun Ge
JOM, 2017, 69 : 1992 - 1996

← 1 2 3 4 5 →