Interface structure and mechanical properties of the brazed joint of TiC cermet and steel

被引：26

作者：

Feng, JC ^{[1
]}

Zhang, LX ^{[1
]}

机构：

[1] Harbin Inst Technol, Natl Key Lab Adv Welding Proc Technol, Harbin 150001, Peoples R China

来源：

JOURNAL OF THE EUROPEAN CERAMIC SOCIETY | 2006年 / 26卷 / 07期

基金：

中国国家自然科学基金;

关键词：

TiC cermet; joining; interfaces; microstructure; strength;

D O I：

10.1016/j.jeurceramsoc.2005.01.043

中图分类号：

TQ174 [陶瓷工业]; TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A commercially available Ag-Cu braze alloy foil with Zn Was Used to join TiC cermet and steel. According to the experimental observations, the interface structure is (Cu, Ni)/Ag (s.s.) + Cu (s.s.)/(Cu, Ni)/(Cu, Ni) + (Fe Ni) from TiC cermet to steel side. With increased brazing temperature or time, the amounts of (Cu, Ni) near the base metals/Ag-31Cu-23Zn interface and (Cu, Ni) + (Fe, Ni) near the Ag-31Cu-23Zn/steel interface increase, while the amount of Ag (s.s.) + Cu (s.s.) in the middle of the braze alloy decreases. The whole joining process consists of diffusion and solution among atoms of the braze alloy foil and base metals. The maximum shear strength is 120.7 MPa for the joint brazed at 850 degrees C for 10 min. (c) 2005 Elsevier Ltd. All rights reserved.

引用

页码：1287 / 1292

页数：6

共 50 条

[21] Interface Characteristics and Mechanical Properties of the Vacuum-Brazed Joint of Titanium-Steel Having a Silver-Based Brazing Alloy
A. Elrefaey
W. Tillmann
Metallurgical and Materials Transactions A, 2007, 38 : 2956 - 2962
[22] Microstructure evolution and mechanical properties of the TiB2-TiC-SiC composite ceramic and Nb brazed joint
Wang, Y.
Zheng, X. Y.
Wei, Y. R.
Yang, Z. W.
JOURNAL OF MANUFACTURING PROCESSES, 2023, 92 : 179 - 188
[23] Interface characteristics and mechanical properties of the vacuum-brazed joint of titanium-steel having a silver-based brazing alloy
Elrefaey, A.
Tillmann, W.
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2007, 38A (12): : 2956 - 2962
[24] Interface structure and mechanical properties of the TiAl/42CrMo steel joint vacuum brazed with Ag-Cu/Ti/Ag-Cu filler metal
Li, Yulong
He, Peng
Feng, Jicai
SCRIPTA MATERIALIA, 2006, 55 (02) : 171 - 174
[25] Brazing temperature and time effects on the mechanical properties of TiC cermet/Ag-Cu-Zn/steel joints
Zhang, L. X.
Feng, J. C.
He, P.
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 428 (1-2): : 24 - 33
[26] Study on the joint mechanical properties of steel structure buildings
Chen, Jiaqiang
INTERNATIONAL JOURNAL OF BUILDING PATHOLOGY AND ADAPTATION, 2021, 39 (04) : 655 - 665
[27] Effect of Bonding Temperature on Microstructure and Mechanical Properties of WC–Co/Steel Diffusion Brazed Joint
Mahdi Shafiei Haghshenas
Nader Parvin
Ali Amirnasiri
Transactions of the Indian Institute of Metals, 2018, 71 : 649 - 658
[28] Mechanical properties of large TiC-Mo-Ni cermet tiles
Agnew, Sean R.
Dong, Liang
Keene, Jasmine, I
Wadley, Haydn N. G.
INTERNATIONAL JOURNAL OF REFRACTORY METALS & HARD MATERIALS, 2018, 75 : 238 - 247
[29] Effect of V content on microstructures and properties of TiC cermet fusion welding interface
魏炜
徐莹
王旭
黄智泉
刘胜新
China Welding, 2024, 33 (01) : 40 - 45
[30] Effects of Mn on the interface bonding and mechanical properties of TiC reinforced steel matrix composites
Li, Jiaxin
Cheng, Minghui
Wang, Chao
Ma, Xuliang
Wang, Xiang
CERAMICS INTERNATIONAL, 2024, 50 (09) : 16650 - 16662

← 1 2 3 4 5 →